PREPARASI DAN KARAKTERISASI KATALIS Co, Mo, CoMo YANG DIEMBANKAN PADA gamma-Al2O3 UNTUK HIDRORENGKAH MINYAK BIJI NYAMPLUNG (Calophyillum InophyillumL) MENJADI BIOFUEL

PUSPA NINDRO MAHAYUWATI, Prof. Dr. Triyono, S.U.; Prof. Dr. Wega Trisunaryanti, M.S.

2018 | Skripsi | S1 KIMIA

Preparasi dan karakterisasi katalis Co, Mo, CoMo yang diembankan pada gamma-Al2O3 untuk hidrorengkah minyak biji nyamplung (Calophyllum Inophyllum L) menjadi biofuel telah dilakukan. Tujuan penelitian ini mempelajari karakter katalis Co/gamma-Al2O3, Mo/gamma-Al2O3, dan CoMo/gamma-Al2O3 dan uji aktivitas katalis pada proses hidrorengkah minyak nyamplung. Penelitian ini dimulai dengan preparasi katalis monometal (Co atau Mo) maupun bimetal (CoMo) yang diembankan pada gamma-Al2O3. Karakterisasi kristanilitas katalis dianalisis dengan X-Ray Diffraction (XRD), kandungan logam katalis dianalisis dengan Atomic Absorption Spectrophotometer (AAS), analisis karakter pori katalis menggunakan Surface Area Analyzer (SAA), serta uji keasaman katalis menggunakan metode gravimetri. Uji aktivitas katalis dilakukan melalui proses hidrorengkah minyak biji nyamplung dengan laju alir gas H2 30 mL menit-1 pada temperatur 550 derajat C selama 2 jam dengan rasio berat katalis dan umpan sebesar 1:100. Produk cair yang dihasilkan dari proses hidrorengkah dianalisis menggunakan GC-MS. Hasil penelitian menunjukkan pengaruh pengembanan logam Co dan Mo pada gamma-Al2O3 tidak merusak struktur gamma-Al2O3 yang berbasis amorf. Keasaman katalis meningkat seiring dengan meningkatnya kandungan logam total yang diembankan pada gamma-Al2O3. Selain itu, pengaruh pengembanan logam menurunkan luas permukaan spesifik katalis gamma-Al2O3, Co10/gamma-Al2O3, Mo10/gamma-Al2O3, Co5Mo5/gamma-Al2O3, dan Co10Mo10/gamma-Al2O3 secara berturut-turut sebesar 127,182; 126,526; 125,767; 122,837; dan 107,665 m2/g. Katalis Co10Mo10/gamma-Al2O3 menunjukkan aktivitas tertinggi dalam menghasilkan produk cair sebesar 65,56% (b/b). Katalis Co5Mo5/gamma-Al2O3 menunjukkan selektivitas terbaik dengan menghasilkan fraksi bensin (gasolin) C6-C12 sebesar 9,11% (b/b) dan fraksi diesel (>C12) sebesar 7,52% (b/b) .

The preparation and characterization of Co, Mo, CoMo supported on gamma-Al2O3 catalysts for hydrocracking of nyamplung seed oil (Calophyllum Inophyllum L) has been conducted. The purpose of this research was to studied characters of Co/gamma-Al2O3, Mo/gamma-Al2O3, and CoMo/gamma-Al2O3 and catalyst activity test in hydrocracking process of nyamplung oil. This research started with preparation of monometal (Co or Mo) catalyst and bimetal (CoMo) catalysts supported on gamma-Al2O3. Crystallinity of the catalysts was analyzed using X-ray Diffraction (XRD), metal contains of catalysts was analyzed using Atomic Absorption Spectrophotometer (AAS), analyzed their pore characters by Surface Area Analyzer (SAA), and their acidity test using gravimetric method. Catalytic activity of catalysts was evaluated in hydrocracking of nyamplung seed oil with H2 gas flow rate 30 mL min-1at 550 degree C for two hours with catalyst to feed weight rasio of (1:100). The liquid products obtained from hydrocarcking process were analyzed using GC-MS. The research results showed that the impregnation of Co and Mo metal on gamma-Al2O3 did not change stucture of gamma-Al2O3 which is amorphous. The acidity of the catalyst increased as the increased of metals contain in supported catalysts. In addition, the metal impregnation decrease the spesific surface area of the catalysts gamma-Al2O3, Co10/gamma-Al2O3, Mo10/gamma-Al2O3, Co5Mo5/gamma-Al2O3, and Co10Mo10/gamma-Al2O3 respectively 127.182; 126.526; 125.767; 122.837; and 107.665 m2/g. The Co10Mo10/gamma-Al2O3 catalyst showed the highest activity by producing a liquid product of 65.56% (w/w). The Co5Mo5/gamma-Al2O3 catalyst showed the best selectivity by generating a C6-C12 gasoline fraction of 9.11% (w/w) and diesel fraction (>C12) of 7.52% (w/w).

Kata Kunci : minyak nyamplung, katalis, hidrorengkah