ZEOLIT-APTMS TERCETAK Cu SEBAGAI ADSORBEN Cu(II) DALAM AIR

TIKA ROMADHONNI, Prof. Dr. Narsito; Dr. Adhitasari Suratman, M.Si

2015 | Tesis | S2 Ilmu Kimia

Telah dilakukan modifikasi zeolit alam dengan senyawa 3-aminopropiltrimetoksisilan melalui proses grafting dan dipelajari aplikasinya untuk adsorpsi ion Cu(II). Zeolit alam dimodifikasi dengan cara menambahkan senyawa aminopropil trimetoksisilan (APTMS) dengan metode grafting menggunakan pelarut etanol dan dalam sistem refluks. Zeolit APTMS tercetak Cu dikarakterisasi dengan menggunakan spektofotometri inframerah untuk mengidentifikasi gugus fungsional dan difraksi sinar-X (XRD). Kajian adsorpsi dilakukan dengan menggunakan sistem batch dengan variasi pH dan konsentrasi ion Cu(II). Model isoterm Langmuir dan Freundlich digunakan untuk menentukan kapasitas dan energi adsorpsi. Hasil penelitian menunjukkan bahwa adsorpsi Cu(II) pada zeolit alam dan zeolit APTMS tercetak Cu optimum pada pH 4, mengikuti model Isoterm Langmuir dengan kapasitas adsorpsi maksimum zeolit alam sebesar 16,80 mg g-1 dan zeolit APTMS tercetak Cu sebesar 34,22 mg g-1. Energi yang dicapai sebesar 24,86 kJ mol-1 untuk zeolit alam dan 30,47 kJ mol-1 untuk zeolit APTMS tecetak Cu.

Natural zeolite was modified with 3-aminopropyl trimethoxysilane compounds through the process of grafting and its application to adsorb Cu(II) was studied. Natural zeolite was modified by adding aminopropyl trimethoxysilane (APTMS) by grafting method using ethanol and the reflux system. zeolite APTMS imprinted Cu was characterized using infrared spektofotometer to identify functional groups and X-ray diffraction (XRD). Adsorption studies was performed using a batch system with variations of pH and ion concentration of Cu(II). Langmuir isotherm and Freundlich models was used to determine the adsorption capacity and energy. The results showed that the optimum conditon of Cu(II) adsorption on natural zeolites and zeolite-APTMS imprinted Cu optimum at pH 4, followed Langmuir isotherm model with a maximum adsorption capacity of natural zeolite was 16.80 mg g-1 and zeolite-APTMS imprinted Cu of 34.22 mg g-1. The energy of 24.86 kJ mol-1 for natural zeolite and 30.47 kJ mol-1 for zeolite APTMS imprinted Cu were reported.

Kata Kunci : Kata kunci : zeolit alam, zeolit-APTMS, adsorpsi, tercetak, grafting, Cu(II)/Natural zeolite, Zeolite-APTMS, adsorption, imprinted, grafting, Cu(II)