SINTESIS KOMPOSIT MATERIAL MAGNETIK/KITOSAN TERIMPREGNASI NANOPARTIKEL PERAK SEBAGAI ANTIBAKTERI Staphylococcus aureus

NIKHO ASYOKA WIJAYA, Prof. Dr.rer.nat. Nuryono, M.S.

2020 | Skripsi | S1 KIMIA

Dalam penelitian ini, komposit material magnetik/kitosan terimpregnasi nanopartikel perak telah disintesis sebagai antibakteri Staphylococcus aureus. Penelitian diawali dengan isolasi material magnetik (MM) dari pasir besi, sintesis komposit material magnetik/kitosan (MM/Kit) dan komposit magnetik/kitosan terimpregnasi nanopartikel perak (MM/Kit/AgNP) dengan variasi konsentrasi larutan AgNO3. Material yang telah disintesis dikarakterisasi dengan spektrofotometer FT-IR, XRD, SEM-EDX dan TEM. Uji antibakteri dilakukan dengan metode difusi sumuran untuk mengetahui diameter zona hambat yang menunjukkan aktivitas antibakteri. Hasil penelitian menunjukkan komposit MM/Kit/AgNP telah berhasil disintesis dan memberikan aktivitas antibakteri yang tinggi terhadap Staphylococcus aureus ditunjukkan dari zona hambat (> 10 mm) dan termasuk kategori kuat. Konsentrasi AgNP yang diimpregnasikan semakin besar pada komposit maka aktivitas antibakterinya meningkat. Komposit MM/Kit/AgNP dengan AgNO3 1,5 mM merupakan komposit yang memiliki aktivitas antibakteri terbesar dengan diameter zona hambat sebesar 16,79 mm.

In this research, synthesis of composite magnetic material/chitosan impregnated with silver nanoparticles as an antibacterial Staphylococcus aureus has been carried out. The research was begun with isolation of magnetic materials (MM) from iron sand, synthesis of magnetic material/chitosan (MM/Kit) composite and magnetic material/chitosan impregnated silver nanoparticles (MM/Kit/AgNP) composite with various concentrations of AgNO3 solution. The materials that have been synthesized were characterized by FT-IR spectrophotometer, XRD, SEMEDX and TEM. Antibacterial test was carried out by using the well diffusion method to determine the diameter of the inhibitory zone indicating antibacterial activity. The results showed that MM/Kit/AgNP composites have been successfully synthesized and provide high antibacterial activity against Staphylococcus aureus as shown from the inhibitory zone (> 10 mm) which is in the strong category. The higher the concentration of AgNP added to the composites, the higher the antibacterial activity. MM/Kit/AgNP with 1.5 mM AgNO3 gave antibacterial activity with a diameter of the inhibition / clear zone of 16.79 mm.

Kata Kunci : material magnetik, kitosan, nanopartikel perak, antibakteri, Staphylococcus aureus