ADSORPSI Cr(VI) MENGGUNAKAN MODIFIKASI BRINE WATER

LENI MARLINA, Dr. Eko Sugiharto, DEA; Dr. Adhitasari Suratman, MSi

2016 | Tesis | S2 Ilmu Kimia

INTISARI Telah dilakukan penelitian modifikasi brine water untuk sintesis Mg/Al hidrotalsit dari brine water (Mg/Al HTB) dan Sintesis Mg/Al hidrotalsit murni (Mg/Al HT). Penelitian ini bertujuan untuk mengetahui kemampuan Mg/Al HTB dan Mg/Al HT dalam mengadsorpsi Cr(VI). Parameter yang digunakan adalah pH optimal, waktu kontak, kinetika adsorpsi, isoterm adsorpsi dan desorpsi. Desorben yang digunakan antara lain aquabides, NaOH 0,01 M dan NaOH 0,1 M. Sintesis Mg/Al HTB dan Mg/Al HT dilakukan dengan metode kopresipitasi pada pH 10 dan hidrotermal selama 15 jam. Hasil yang diperoleh, dikarakterisasi menggunakan XRD dan FTIR (Fourier Transfrorm Infrared Spectroscopy). Konsentrasi Cr(VI) ditentukan dengan metode difenilkarbazid menggunakan spektrofotometer UV-Vis pada λoptimal 542 nm. Hasil penelitian menunjukkan bahwa Mg/Al HTB dan Mg/Al HT mampu mengadsoprsi Cr (VI) pada pH optimal 4, waktu kontak 150 menit, mengikuti kinetika reaksi pseudo orde dua. Isoterm adsorpsi Mg/Al HTB dan Mg/Al HT mengikuti Isoterm Langmuir dengan kapasitas adsorpsi untuk Mg/Al HTB 40,65 mg/g dan Mg/Al HT 58 mg/g. Cr(VI) terdesorpsi optimal menggunakan NaOH 0,1 M diperoleh prosentase terdesorpsi 82,83 % untuk Mg/Al HTB dan 54,9% dengan Mg/Al HT.

ABSTRACT The research on modified of brine water for synthesis of brine water Mg/Al hydrotalcite (Mg/Al HTB) from desalination power plant and pure Mg/Al hydrotalcite (Mg/Al HT) has been conducted. This research aims to determine the capability of Mg/Al HTB and Mg/Al HT to adsorb Cr(VI). Parameters were observed such us pH, contact time, adsorption kinetic, adsorption isotherm and desorption. The desorbed agent consists of distilled water, 0.01 M of NaOH, 0.1 M of NaOH. The synthesis of Mg/Al HTB and Mg/Al HT were conducted using co-precipitation method at pH of 10 and continued hydrothermal process for 15 hours. The obtained samples were characterized using XRD and FTIR (Fourier Transfrorm Infrared Spectroscopy). The concentration of Cr(VI) was determined by diphenylcarbazide method using UV-Vis Spectrophotometer at 542 nm. The results showed that Mg/Al HTB and Mg/Al HT able to adsorb Cr(VI) at pH 4, 150 minutes and followed the second order pseudo reaction kinetics. The adsorption isotherm of Mg/Al HTB and Mg/Al HT using Langmuir Isotherm with adsorption capacity 40.65 mg/g and 58 mg/g respectively. The Cr(VI) was desorbed optimally by NaOH 0.1M and obtained the desorption percentage of Mg/Al HTB and Mg/Al HT respectively 54.9% and 82.83%.

Kata Kunci : hidrotalsit, brine water, adsorpsi, Cr(VI)