UJI KOEFISIEN SERAPAN RADIASI BAHAN KOMPOSIT GLASS-FIBER REINFORCED CEMENT (GRC) MENGGUNAKAN RADIOGRAFI SINAR-X DIGITAL

ADDINIYAL HIKMAH, Dr Gede Bayu Suparta

2016 | Tesis | S2 Ilmu Fisika

Pengujian koefisien serapan radiasi bahan komposit Glass-Fiber Reinforced Cement (GRC) menggunakan radiografi sinar-X digital telah dilakukan. Penelitian ini dilakukan untuk mengetahui kemampuan bahan komposit GRC dalam menyerap radiasi jika digunakan sebagai bahan perisai radiasi. Perisai radiasi diperlukan untuk membatasi agar paparan radiasi tidak menyebar keluar dari lokasi penggunaannya. Pengujian dilakukan terhadap komposit GRC dengan variasi ketebalan bahan 4 mm, 6 mm dan 8 mm. Alumunium digunakan sebagai bahan pembanding komposit. Hasil pengujian dengan menggunakan energi sinar-X sebesar 70 keV diperoleh nilai koefisien serapan komposit GRC untuk ketebalan 4 mm, 6 mm dan 8 mm berturut-turut sebesar (0,027 ± 0,003) mm-1, (0,025 ± 0,002) mm-1 dan (0,023 ± 0,002) mm-1. Komposit GRC ketebalan 12 mm ekuivalen terhadap alumunium ketebalan 6 mm dalam mereduksi radiasi. Namun, komposit GRC baru dapat digunakan sebagai alternatif perisai radiasi bila ketebalannya minimal 277,2 mm.

Testing on radiation absorption coefficient of Glass-Fiber Reinforced Cement (GRC) composite material using X-ray digital radiography has been conducted. This research aims to find out the ability of the composite material in absorbing the radiation so that it may be used as a radiation shield. Radiation shield is necessary to reduce the radiation exposure spread out of the area. Tests on radiation absorption coefficient were conducted on GRC composite with variations in material thickness of 4 mm, 6 mm and 8 mm. Aluminum was used as a reference. The result when using X-ray energy of 70 keV showed that the absorption coefficient of the GRC composite with a thickness of 4 mm, 6 mm and 8 mm were (0,027 ± 0,003) mm-1, (0,025 ± 0,002) mm-1 dan (0,023 ± 0,002) mm-1 consecutively. The GRC composite thickness of 12 mm was equivalent to aluminum thickness of 6 mm in reducing radiation. However, the GRC composite may be used as radiation shielding when its thickness at least 277,2 mm.

Kata Kunci : radiasi sinar-X, komposit, koefisien serapan radiasi, perisai radiasi.