PENGARUH SUHU DAN WAKTU KARBONISASI TERHADAP SIFAT FISIKA - KIMIA BRIKET ARANG DARI LIMBAH SERBUK GERGAJI KAYU MINDI (Melia azedarach L.)

ANINDYA HUSNUL HASNA, Dr. Ir. J. P. Gentur Sutapa, M.Sc.

2016 | Skripsi | S1 KEHUTANAN

Limbah dari industri penggergajian berupa serbuk gergaji Mindi belum dimanfaatkan secara optimal. Penelitian ini bertujuan untuk memanfaatkan dan mengolah limbah serbuk gergajian Mindi (Melia azedarach L.) menjadi salah satu sumber energi terbarukan berupa briket arang, serta mengetahui pengaruh variasi suhu dan waktu karbonisasi, dan kombinasi suhu dan waktu karbonisasi yang optimal pada pembuatan briket arang dari limbah serbuk gergaji kayu Mindi (Melia azedarach L.). Limbah serbuk gergajian Mindi (Melia azedarach L.) berasal dari industri gergajian UD. Tonoputro dan UD. Sambisari Desa Cangkringan, Kabupaten Sleman, Provinsi D.I.Y. Penelitian ini menggunakan rancangan acak lengkap (Completely Randomized Design) dengan 2 faktor perlakuan yaitu suhu karbonisasi (300oC, 350oC, dan 400oC) dan waktu karbonisasi (2,5 jam, 3 jam, dan, 3,5 jam) dengan masing-masing perlakuan lima kali ulangan. Pada proses pembuatan briket arang dilakukan dengan cara penambahan bahan perekat yang dibuat dengan perbandingan 1:16 dengan arang yang sudah ditumbuk sebanyak 27 gram kemudian dicetak dengan sistem hidrolik manual selanjutnya dikeringkan. Briket arang yang dihasilkan diuji kualitasnya yaitu sifat fisik (kadar air, berat jenis, dan nilai kalor) dan sifat kimia (kadar abu, kadar zat mudah menguap, dan kadar karbon terikat). Hasil penelitian menunjukkan briket arang yang dihasilkan memiliki sifat-sifat sebagai berikut : kadar air 3,59 - 6,41%; berat jenis 0,53-0,75; nilai kalor 5.213,94-7.643,97 kal/g; kadar abu 4,42 - 5,45%; kadar zat mudah menguap 19,66 - 41,89%; dan karbon terikat 47,38 - 71,37%. Briket arang kualitas terbaik didapatkan pada kombinasi suhu karbonisasi 350oC dengan waktu karbonisasi 3,5 jam yang menghasilkan briket arang dengan spesifikasi : kadar air 5,61%; berat jenis 0,73; nilai kalor 7.642,97 kal/g; kadar abu 5,12%; kadar zat mudah menguap 41,89%; dan karbon terikat 47,38%. Hasil pengujian kadar air, nilai kalor, dan kadar abu briket arang memenuhi standar perdagangan briket Jepang, Amerika, dan SNI.

Sawdust of Mindi wood waste wich was resulted as by product of sawmilling process was not used optimally, although the waste was quite abundant. The aims of this research were utilizing and processing waste of sawdust of Mindi (Melia azedarach L.) became one of renewable energy resources as Charcoal Briquette; procuring new information abaout the influence of variation of temperature and duration of carbonization; an optimal combination between temperature and duration of carbonization in charcoal briquettes making from sawdust of Mindi wood (Melia azedarach L.). Sawdust of Mindi wood (Melia azedarach L.) was collected from sawmills UD. Tonoputro and UD. Sambisari, Desa Cangkringan, Sleman, D.I.Yogyakarta. in this research was applied Completely Randomized Design, treated by 2 factors, there were temperature variation of carbonization (300oC, 350oC and 400oC) and duration of carbonization (2.5 hours, 3 hours, and, 3.5 hours). Each treatment had five repetitions. At process of charcoal briquette was done by agglutinant addition made with the comparison 1:16 with the crushed charcoal as much 27 gram, then printed with the manual hydraulic system dried. Quality of charcoal briquettes, physical properties (moisture content, specific gravity and heating value) and chemical properties (ash content, volatile matter content, and fixed carbon). The results shows that the properties of charcoal briquette in this research are : moisture content of 3.59-6.41%; specific gravity 0.53-0.75; heating value 5213.94-7643.97 cal/g; ash content 4.42-5.45%; volatile matter content 19.66-41.89%; and fixed carbon content 47.38-71.37%. The best charcoal briquette is obtained from combination temperature of carbonization 350oC and duration of carbonization 3.5 hours with the properties : moisture content 5.61%; specific gravity 0.73; heating value 7642.97 cal/g; ash content 5.12%; volatile matter content 41.89%; and fixed carbon 47.38%. The testing results of moisture content, heating value and ash content of charcoal briquettes is fullfiled the conditions charcoal briquette standard trading for Japan, America, and SNI.

Kata Kunci : Limbah Serbuk Gergaji Mindi, Briket Arang, Suhu Karbonisasi, Waktu Karbonisasi, Sifat Fisika-Kimia