FOTOREDUKSI ION Cr(VI) TERKATALIS TiO2-LIGNIN

YUNIAR, Prof. Dr. Endang Tri Wahyuni, MS ; Dr. rer. nat. Nurul Hidayat Aprilita, M.Si

2016 | Tesis | S2 Ilmu Kimia

Dalam rangka peningkatan aktivitas TiO2 telah dilakukan preparasi dan karakterisasi TiO2-lignin sebagai fotokatalis dan uji aktivitasnya pada fotoreduksi ion Cr(VI) dalam larutan. Preparasi dilakukan dengan cara menginteraksikan serbuk TiO2 yang telah disuspensikan dalam air-etanol dengan serbuk lignin dengan pengadukan tetap selama 24 jam, diikuti dengan kalsinasi pada temperatur 400 °C. Karakterisasi dilakukan dengan alat Difraktometer Sinar-X (XRD) dan FT-IR. Uji aktivitas TiO2-lignin pada fotoreduksi ion Cr(VI) dilakukan dengan reaktor sistem batch. Pada tahap uji ini telah dipelajari pengaruh kadar TiO2 dalam TiO2-lignin, waktu penyinaran, massa fotokatalis, dan konsentrasi awal Cr(VI) terhadap efektivitas fotoreduksi. Hasil penelitian menunjukkan bahwa pendispersian TiO2 pada lignin memberikan aktivitas fotokatalis pada fotoreduksi Cr(VI) yang lebih besar daripada TiO2. Kenaikan kadar TiO2 dalam TiO2-lignin memberikan fotoreduksi Cr(VI) yang semakin besar dan mencapai maksimum pada rasio massa TiO2/ lignin 2:1. Waktu penyinaran yang semakin lama, massa fotokatalis TiO2-lignin dan konsentrasi ion Cr(VI) yang semakin besar menghasilkan reduksi Cr(VI) yang semakin besar, dan kondisi optimum dicapai pada waktu 40 jam dan pada penggunaan massa 50 mg serta konsentrasi Cr(VI) 1 mg/L, dengan hasil fotoreduksi ion Cr(VI) sebesar 81,44%.

In order to increase the activity of TiO2, preparation and characterization of TiO2-lignin and the activity study for Cr(VI) photoreduction have been carried out. The preparation was done by interacting TiO2 powder suspended in water-ethanol with lignin powder accompanied by stirring for 24 h, followed by calcination at 400°C. The Characterizations were performed by X-ray diffraction (XRD) and FT-IR. The photoreduction of Cr(VI) was conducted by a batch system reactor. The effect of TiO2 content in the TiO2-lignin, irradiation time, mass of photocatalyst and initial concentration of Cr(VI) on the effectiveness of photoreduction have also been studied. The results showed that the activity of TiO2-lignin on the photoreduction of Cr(VI) was higher than TiO2. Increasing TiO2 content in the TiO2-lignin gave higher Cr(VI) photoreduction and reached a maximum photoreduction with TiO2-lignin mass ratio of TiO2/lignin 2:1. The extension of the irradiation time, the higher mass of TiO2-lignin photocatalyst and the increase of the initial concentration of Cr(VI) resulted in the increase of Cr(VI) reduction, which reached a maximum result at 40 h, 50 mg of TiO2-lignin and the concentration of Cr(VI) 1 mg/L with percent reduction of Cr(VI) was 81.44%.

Kata Kunci : TiO2-lignin, Cr(VI) ion, photoreduction