PENGARUH PENCUCIAN ABU VULKANIK GUNUNG KELUD DENGAN MENGGUNAKAN LARUTAN Na2EDTA TERHADAP KAPASITAS ADSORPSI PADA ION Pb(II)

CITRA AYU WIDYA N., Prof. Dr. Endang Tri Wahyuni, M.S;Dr. rer.nat. Adhitasari Suratman, S.Si., M.Si

2016 | Skripsi | S1 KIMIA

Untuk meningkatkan kapasitas adsorpsi abu vulkanik Gunung Kelud, telah dilakukan penghilangan logam-logam pengotor berupa Ca, Mg dan Fe dengan metode disolusi menggunakan larutan garam EDTA. Penelitian ini diawali dengan mengkarakterisasi abu vulkanik Gunung Kelud dengan XRD dan AAS untuk mengetahui komposisi mineral dan komposisi kimia. Langkah kedua berupa proses disolusi oksida logam Ca, Mg dan Fe dalam abu vulkanik dengan cara mengaduk campuran abu vulkanik dengan larutan garam EDTA. Untuk memperoleh hasil pelarutan yang maksimum telah dipelajari pengaruh konsentrasi larutan garam EDTA terhadap jumlah logam-logam oksida yang terdisolusi. Konsentrasi Ca, Mg dan Fe yang terlarut dalam larutan EDTA kemudian dianalisis dengan AAS. Tahap selanjutnya adalah adsorpsi ion Pb(II) dengan abu vulkanik yang telah terdisolusi dengan melakukan optimasi waktu kontak dan pH. Hasil penelitian menunjukkan bahwa konsentrasi optimum larutan EDTA dalam disolusi abu vulkanik adalah 0,1 M yang dapat melarutkan logam Ca 39,94 mg/g, Mg 4,80 mg/g, dan Fe 4,16 mg/g. Pada proses adsorpsi ion Pb(II) dengan abu vulkanik tergantung pada waktu kontak 60 menit dan pH 6. Kapasitas adsorpsi abu vulkanik mengalami kenaikan setelah didisolusi dengan larutan Na2EDTA yaitu sebesar 51,55 mg Pb/g-abu vulkanik dari 23,09 mg Pb/g-abu vulkanik. Kata kunci: disolusi, konsentrasi larutan EDTA, waktu kontak, pH.

In order to increase the adsorption capacity of volcanic ash from Gunung Kelud, removing of Ca, Ma and Fe oxides as impurities has been carried out by dissolution method using EDTA-salt solution. This research was initiated by characterization of the volcanic ash using XRD and AAS to find out types of minerals and the chemical composition. Second step was dissolution process of Ca, Mg and Fe oxides from the volcanic ash conducted by stirring suspensions consisting of the volcanic ash and EDTA solution. To obtain maximum result of the dissolution, the effect of concentration of EDTA solution on the result of Ca, Mg and Fe oxides dissolution from volcanic ash has been studied. The concentration of Ca, Ma and Fe dissolved in the EDTA solution were determined by AAS. The results of the research showed that the optimum concentration of EDTA solution was 0,1 M for dissolution volcanic ash that can dissolve Ca 39.94 mg/g, Mg 4.80 mg/g, and Fe 4.16 mg/g. The adsorption Pb(II) ion by volcanic ash was found to be influenced by the contact time and the pH and the optimum time and pH were 60 minutes and 6. Adsorption capacity of volcanic ash increased after dissolution using Na2EDTA solution into 51.55 mg Pb/g- volcanic ash from 23.09 mg Pb/g- volcanic ash. Key words: dissolution, concentration of EDTA solution, contact time, pH.

Kata Kunci : disolusi, konsentrasi larutan EDTA, waktu kontak, pH.