SINTESIS KOMPOSIT ZEOLIT MAGNETIT SEBAGAI ADSORBEN CEPAT PISAH ION Cd2+

TRISATYA M BAKARA , Dr. Suyanta, M.Si; Prof. Dr. Iip Izul Falah

2016 | Skripsi | S1 KIMIA

Telah dilakukan sintesis komposit zeolit-magnetit untuk memperoleh adsorben yang memiliki sifat kemagnetan serta aplikasinya untuk adsorpsi ion Cd2+. Untuk membuat komposit tersebut, sebanyak 2,0 g serbuk zeolit teraktivasi dimasukkan ke dalam campuran larutan yang mengandung Fe2+ dan Fe3+ dengan perbandingan mol 1:2. Larutan NH4OH ditambahkan ke dalam campuran hingga pH 11,0 pada temperatur 85 derajat Celcius. Endapan yang terbentuk selanjutnya disaring, dicuci dan dikeringkan pada temperatur 100 derajat Celsius selama 1 jam. Komposit zeolit-magnetit kemudian dikarakterisasi dengan menggunakan spektrometer inframerah, difraksi sinar-x dan fisisorpsi Nitrogen. Dalam penelitian ini, padatan hasil sintesis digunakan untuk mengadsorp logam Cd2+ dalam larutan pada pH 5,0. Konstanta laju adsorpsi (k) dan stabilitas (K) dipelajari dengan menggunakan model kinetika pseudo orde dua Ho dengan tetapan laju adsorpsi 1,55 g/mg menit. Uji recovery pasca aplikasi fasa padat menggunakan komposit zeolit-magnetit memerlukan waktu yang lebih cepat dibanding zeolit teraktivasi.

The synthesis zeolite-magnetite composite to obtain adsorbent having magnetic property and its application to the adsorption of Cd2+ ion has been performed. Two grams of activated natural zeolite powder were added into a solution containing a mixture of Fe2+ and Fe3+ with a molar ratio of 1: 2. Solution of NH4OH was added to the mixture to achieved pH as high as 11.0 at 85 Celcius degree. The formed precipitate was filtered, washed and dried at 100 celcius degree for 1 hour. Zeolite-magnetite composite then was characterized using infrared spectrometer, x-ray diffractometer and nitrogen autosorption. The product of the synthesis were used to adsorp Cd2+ in the solutions at pH 5.0. The rate (k) and stability (K) constants were studied using pseudo second-order kinetic model where the rate constant of adsorption was found to be 1.55 g/mg min. Recovery test after its application showed that the zeolite-magnetite composite required a faster time than the activated zeolite.

Kata Kunci : zeolit, komposit zeolit-magnetit, kopresipitasi, adsorpsi.