HIDRORENGKAH MINYAK JARAK (Ricinus communis l.) MENGGUNAKAN KATALIS Cr-Al2O3/ BENTONIT

ANI DEVI ARI YANTI, Prof. Dr. Karna Wijaya, M.Eng; Drs. Iqmal Tahir, M.Si

2016 | Skripsi | S1 KIMIA

Sintesis dan karakterisasi Cr-Al2O3/bentonit untuk reaksi hidrorengkah minyak jarak (Ricinus communis L.) menjadi biogasolin telah dilakukan. Lempung alam diaktivasi menggunakan H2SO4 sehingga diperoleh H-bentonit. Pilarisasi bentonit menggunakan ion Keggin Al13 sebagai agen pemilar. Preparasi katalis Cr-Al2O3/bentonit dilakukan dengan metode impregnasi larutan garam prekursor Cr(NO3)3•9H2O pada sampel bentonit terpilar, dilanjutkan dengan kalsinasi dan reduksi, sehingga diperoleh katalis Cr-Al2O3/bentonit. Katalis yang diperoleh dikarakterisasi dengan spektrometer inframerah (FT-IR), Difraktometer Sinar-X (XRD), X-ray Fluorescence Spectrometer (XRF) dan Transmission Electron Microscope (TEM). Luas permukaan spesifik, rerata jejari pori serta volume pori dianalisis menggunakan gas sorption analyzer (BET). Produk hidrorengkah dianalisis dengan GC-MS. Hasil penelitian menunjukkan bahwa pada proses pilarisasi bentonit menggunakan oksida aluminium (Al2O3) sebagai ion Keggin dapat meningkatkan basal spacing sebesar 1,97 nm dengan Δd001 sebesar 1,01 nm. Walaupun logam Cr tidak terdispersi secara merata yang menyebabkan luas permukaannya menurun, namun katalis Cr-Al2O3/bentonit menghasilkan konversi produk cair yang paling besar yaitu 64,03% karena memiliki situs asam yang paling tinggi sebesar 8,26 mmol amonia/g. Data GC-MS menunjukkan senyawa yang terkandung dalam produk hidrorengkah adalah aseton, asam asetat, metil benzena, oktana, heptanal, 2-oktanon, asam 1-undekanoat, asetamida, 9-oktadekanal dan asam 10-undecenoic.

Synthesis and characterization of biogasoline from castor oil (Ricinus communis L.) have been conducted using Cr-Al2O3/bentonite as the catalyst. Natural clay was activated using H2SO4 in order to obtain H-bentonite. Pillarization conducted using Al13 Keggin ion as pillaring agent. Precursor salt solution Cr(NO3)3•9H2O was impregnated in pillared bentonite samples, followed by calcination and reduction in order to obtain the final catalyst, Cr-Al2O3/bentonite. The catalysts were characterized using infrared spectrometer (FT-IR), X-Ray diffraction (XRD), X-ray Fluorescence spectrometer (XRF) and Transmission Electron Microscope (TEM). Specific surface area, average pore size and total pore volume were analyzed using gas sorption analyzer (BET). The final product was characterized by using GC-MS. The research results showed that bentonite pillarization using aluminum oxide (Al2O3) as Keggin ion increased basal spacing by 1.97 nm with Δd001 by 1.01 nm. Although Cr was uneven dispersed causing a decrease in specific surface area, Cr-Al2O3/bentonite catalyst gives the best biogasoline conversion of 64.03% because it had the highest acid site by 8.26 mmol ammonia/g. The GC-MS data showed that the hydrocracking products contained of acetone, acetic acid, methyl benzene, octane, heptanal, 2-octene, 1-undecanoic acid, 9-octadecenal and 10-undecanoic acid.

Kata Kunci : katalis krom, bentonit, hidrorengkah, minyak jarak, biogasolin