TUGAS AKHIR STUDI PEMBUATAN BETON RINGAN NON AAC (Non-Autoclaved Aerated Concrete) DENGAN BAHAN TAMBAH HIDROGEN PEROKSIDA DAN MILL

DERIZA DEBY DWIANTO, Edi Kurniadi, ST., MT;Lava Himawan, ST.,MT.;Agus Kurniawan, ST.,Ph.D

2016 | Tugas Akhir | D3 TEKNIK SIPIL SV

Perkembangan dunia konstruksi di Indonesia ikut mendorong betambahnya penggunaan beton sebagai material perkuatan struktur. Bata ringan saat ini dikenal ada 2 (dua) jenis yaitu Autoclaved Aerated Concrate (AAC) dan Celluler Lightweight (CLC). CLC sering disebut juga beton Non-ACC (Autoclaved Aerated Concrate). Dimana beton yang dimatangkan tanpa autoclave ini belum banyak dikomersialkan dibanding beton ringan AAC. Penelitian ini di titik beratkan pada hasil kuat tekan, dan porositas. Beton ringan yang di pakai penelitian ini adalah Non-ACC (Autoclaved Aerated Concrate) dengan bahan penyusun yang meliputi air, pasir, semen mill,cairan pengeras SikaCim, dan Hidrogen peroksida. Dengan focus pada metode pengadukan yang sangat berpengaruh pada hasil 4 uji trial, kemudian ditetapkan pada trial ke 4 sebagai benda uji dan koefisien Water/cement (w/c): 0,40, Sand/Cement ( s/c ): 0.75, H2O2:0.1, mill/ Cement (%): 0.5. Kemudian pengujian yang dilakukan yaitu uji kuat tekan ,porositas dan uji berat jenis Pada hasil uji kuat tekan campuran beton ringan yang berjumlah 9 eksperimen rata-rata nilai kuat terkan tertinggi diperoleh pada BRD-06 dengan nilai 2 MPa. Dan rata-rata nilai kuat tekan terendah di peroleh pada eksperimen BRD-09 yaitu 0,97 MPa. Porositas tertinggi didapat pada eksperimen BRD-01 dengan nilai 23,88% dan porositas terendah di dapat pada eksperimen BRD-06 dengan nilai 15,04%. Hasil rata-rata nilai berat jenis dengan nilai tertinggi di dapat dari eksperimen BRD-06 yaitu dengan nilai 1083,7 kg/m3 dan nilai terendah diperoleh oleh eksperimen BRD-01 dengan nilai 902,7 kg/m3.

The development of construction in Indonesia contributed to the increasing use of concrete as a structural reinforcement material. Light brick is now known there are two (2) types Aerated autoclaved Concrate (AAC) and Celluler Lightweight (CLC). CLC is often referred to concrete Non-ACC (autoclaved Aerated Concrate). Where no autoclave cured concrete has not been widely commercialized lightweight concrete than AAC. This study emphasized on the results of compressive strength and porosity. Lightweight concrete in this study is the use of Non-ACC (autoclaved Aerated Concrate) the constituent material which includes water, sand, cement mill, liquid hardener SikaCim, and hydrogen peroxide. With the focus on the method of stirring a very influential on the results of four test trial, then the trial is set to 4 as a test object and a coefficient of water / cement (w / c): 0,40, Sand / Cement (s / c): 0.75, H2O2 : 0.1, mill / Cement (%): 0.5. Later tests performed that test compressive strength, porosity and density test. In the test results of compressive strength of lightweight concrete mixtures totaling 9 experiments average the highest compressive strength values obtained at BRD-06 with a value of 2 MPa. And the average value of the lowest compressive strength obtained in experiments BRD-09 is 0.97 MPa. The highest porosity obtained in experiments BRD-01 with a value of 23.88% and porosity can be the lowest in the experiment BRD-06 with a value of 15.04%. The average yield specific gravity value with the highest values obtained from experiments BRD-06 is the value of 1083.7 kg / m3 and the lowest value obtained by experiments BRD-01 with a value of 902.7 kg / m3.

Kata Kunci : beton ringan, NAAC, Hidrogen peroksida