Hidrorengkah Minyak Goreng Bekas Dengan Menggunakan Katalis Cr/Bentonit

RONALD MANDEY, Prof. Dr. Karna Wijaya, M.Eng

2016 | Tesis | S2 Ilmu Kimia

Telah dilakukan preparasi, karakterisasi, dan uji aktivitas Cr/Bentonit untuk hidrorengkah minyak goreng bekas. Na/bentonit diaktivasi dengan H2SO4 1 M sehingga diperoleh H/bentonit. Preparasi katalis Cr dilakukan dengan metode impregnasi larutan garam prekursor Cr(NO3)3·9H2O pada sampel H/bentonit, dilanjutkan dengan kalsinasi dan reduksi, sehingga diperoleh katalis Cr/bentonit. Cr/Bentonit yang diperoleh dikarakterisasi dengan FT-IR, Difraktometri Sinar-X (XRD), dan Surface Area Analyzer. Katalis Cr/Bentonit digunakan untuk hidrorengkah minyak goreng bekas dengan variasi rasio katalis/umpan 1/10, 1/15, 1/20 pada suhu 450oC dan laju alir H2 20mL/menit selama 1 jam. Produk hidrorengkah dianalisis dengan GC-MS untuk mengetahui kandungan dan komposisi senyawanya. Hasil penelitian menunjukkan bahwa terjadi penurunan luas permukaan disaat aktivasi dan setelah diimpregnasi logam Cr dari 47,30 m2/g menjadi 19,76 m2/g. Senyawa yang terkandung dalam produk hidrorengkah adalah asam dodekanoat, 9-asam heksadekanoat, dan 9-asam oktadekanoat.

Preparation, characterization and catalytic activity testing of Cr-bentonite for the hydrocracking reaction of used cooking oil have been done. Cr-bentonite preparation began by reacting Na-bentonite with 1 M H2SO4 to obtain of the Hbentonite. Cr-bentonite catalyst preparation was performed through impregnation ofCr(NO3)3·9H2O into H-bentonite, followed by calcination and reduction, in order to obtain Cr-bentonite catalyst. Cr/bentonite obtained was then characterized by FT-IR spectrophotometry, X-ray diffractometry (XRD), porosimetry methods. Cr/bentonite catalyst which was used for hydrocracking of used cooking oil with variation ratio of catalyst/feed 1/10, 1/15, 1/20 at a temperature of 450oC and the flow rate H2 of 20 mL/minute for 1 hour. Hydrocracking product were analyzed by GC-MS to determine the content and composition of the compounds. `The results showedthat the catalyst preparation did not affect the structure of bentonite, however caused a decrease in surface area of bentonite as a result of activation and after Cr impregnationfrom47.30m2/g to19.76m2/ g. Hydrocracking experiment demonstrated that compounds contained in the hydrocracking products were dodecanoic, 9-hexadecenoic acid, and 9-octadecanoic acid.

Kata Kunci : Cr/Bentonit, Hidrorengkah, Minyak goreng bekas