Sintesis TiO2 Tabung Nano Terdoping N dengan Refluks

FITRI RIZKI AMALIA, Dr. Indriana Kartini, M. Si; Dr. Yateman Arryanto

2015 | Skripsi | S1 KIMIA

Telah dilakukan sintesis TiO2 tabung nano terdoping N dengan menggunakan metode refluks sebagai metode doping. Tujuan dari penelitian yaitu untuk mengetahui pengaruh pengaruh perlakuan asam sebagai perlakuan awal sebelum pendopingan N terhadap morfologi, fasa kristalin, dan doping N. Titanat nanotube dengan menggunakan metode hidrotermal kemudian hasil yang diperoleh dibagi menjadi 2 kelompok, kelompok pertama diberikan perlakuan asam dan kelompok kedua tidak dilakukan perlakuan asam. Sampel-sampel tersebut selanjutnya dilakukan doping N dengan metode refluks. Karakterisasi yang dilakukan menggunakan instrumen XRD (X-Ray Diffraction), TEM (Transmission Electron Microscope), FT-IR (Fourrier Transform-Infra Red), GSA (Gas Sorption Analyzer), dan DR-UV-vis (Diffuse Reflectance-Ultra Violet-visible). Hasil penelitian menunjukkan bahwa perlakuan asam berpengaruh dalam meningkatkan pembentukan fasa kristal anatase namun menyebabkan runtuhnya morfologi tabung nano saat dilakukan kalsinasi. Selain itu, perlakuan asam dapat menghalangi pendopingan N. Energi celah pita pada sampel dengan perlakuan asam yaitu 3,20 eV dan sampel tanpa perlakuan asam yaitu 3,17 eV. Luas permukaan spesifik dari sampel hasil pendopingan dengan morfologi tabung nano yaitu 106,07 m2 g-1 dan diameter porinya sekitar 3,75 dan 15,65 nm.

Nitrogen-doped TiO2 nanotube has been synthesized by a reflux as doping method. The aim of this research is to study the effect of acid treatment as a pretreatment of doping method on morphology, crystalline phase, and nitrogen doping. Titanate nanotubes were synthesized by hydrotermal method then the sample was divided into 2 groups, the first group was treated by acid and the second group was not treated by acid. After that, these samples have been doped by N via reflux method. These samples were characterized by XRD (X-Ray Diffraction), TEM (Transmission Electron Microscope), FT-IR (Fourrier Transform-Infra Red), GSA (Gas-Sorption Analyzer), and DR-UV-vis (Diffuse Reflectanceâ-Ultra Violet-visible). The results showed that acid treatment had a significant effect on anatase phase formation but it could destroy the nanotubular into nanorod morphology. Furthermore, acid treatment could prevent the N doping. The energy band gap of the sample with acid treatment is 3.20 eV and the sample without acid treatment is 3.17 eV. The specific surface area of the doping sample with nanotubular morphology is 106.07 m2 g-1 and the pore diameters are about 3.75 and 15.65 nm.

Kata Kunci : TiO2, tabung nano, doping, nitrogen.