NASKAH PUBLIKASI SINTESIS NANOFIBER POLIVINIL ALKOHOL/KITOSAN/IOTA-KARAGINAN SEBAGAI ADSORBEN Pb(II) DAN Cu(II) SYNTHESIS OF POLYVINYL ALCOHOL/CHITOSAN/IOTA-CARRAGEENAN NANOFIBER FOR THE ADSORBENT OF Pb(II) AND Cu(II) ANSELMUS BOY BAUNSELE 13/355384/PPA/04348 PROGRAM STUDI KIMIA DEPARTEMEN KIMIA FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS GADJAH MADA YOGYAKARTA 2015

ANSELMUS BOY B., Drs. Dwi Siswanta, M.Eng., Ph.D; Prof. Drs. Mudasir, M.Eng., Ph.D

2015 | Tesis | S2 Ilmu Kimia

Sintesis nanofiber dengan bahan dasar PVA/kitosan/iota-karaginan telah berhasil dilakukan. Sintesis nanofiber menggunakan metode electrospinning dengan rasio volume bahan PVA/kitosan/iota-karaginan (8:1:1) dan konsentrasi 15%:1%:1%. Nanofiber yang telah disintesis kemudian dikarakterisasi menggunakan FTIR, SEM, uji daya serap air dan ketahanan dalam medium asam.Pengaruh pH, waktu kontak, variasi konsentrasi, kinetika adsorpsi, isoterm adsorpsi, kajian desorpsi, penentuan konstanta adsorpsi dan energi adsorpsi merupakan parameter yang dikaji.Hasil analisis FTIR nanofiber menunjukkan adanya puncak 1605 cm-1, 849 cm-1 dan 1728 cm-1 akibat vibrasi berturutâ-turut dari -NH2,-OSO3- dan O-C-NH2. Hasil karakterisasi SEM menampilkan terbentuknya hasil sintesis nanofiber PVA/kitosan/iota-karaginan. Untuk Pb(II), adsorpsi optimum pada pH 5, waktu kontak 30 menit dan konsentrasi optimum adalah 175 mg L-1. Adsorpsi Cu(II) pada pH 6, waktu kontak 50 menit dan konsentrasi optimum pada 40 mg L-1. Adsorpsi Pb(II) mengikuti isoterm Langmuir dengan kapasitas optimum adalah 21 mg g-1 dengan nilai konstanta (K) sebesar 1505,455L mol-1 dan energi adsorpsi 18,25 kJ mol-1, sedangkan untuk Cu(II), kapasitas adsorpsi adalah 5,7 mg g-1 dengan nilai K adalah 1086,1L mol-1, energi adsorpsi 17,4 kJ mol-1dan mengikuti isoterm Langmuir. Selain adsorpsi, kajian desorpsi untuk kedua ion logam diperoleh hasil bahwa desorpsi dengan natrium-EDTA memiliki persentase desorpsi lebih besar diikuti HNO3, KNO3 dan aquabides.

A research about nanofiber synthesis of polyvinyl alcohol/chitosan/iota-carrageenan nanofiberhas done. Nanofibersynthesishas been obtained by electrospinning method using a composite of PVA:chitosan:iota-carrageenan (8:1:1) of volume ratio with15%:1%:1% of the concentration. The nanofiber which synthezied characterized by FTIR, SEM, water absorption and medium acidity. Another parametersaseffect of pH,contact time, variation of concentration, kinetics adsorption, adsorption isotherms, study of desorption, adsorption constants determination and energy adsorption was studied.The FTIR results showed peakof spectraat 1605 cm-1, 849 cm-1 and 1728 cm-1indicated the-NH2, -OSO3- and O-C-NH2vibrations respectively. The SEM results showed that the polyvinyl alcohol/chitosan/iota-carrageenan nanofiber has been successfully synthesized.Adsorption of Pb(II) was done at optimum pH of 5, for contact time of 30 minutes and the optimum concentration was at 175 mg L-1. The adsorption of Cu(II) was at pH 6,contact time of50 minutes and the optimum concentration of 40 mg L-1. Adsorption of Pb(II)followed Langmuir isotherm with adsorption capacity of 21 mg g-1, adsorption constant (K) of 1505,455 L mol-1 and adsorption energy of 18,25 kJ mol-1. ForCu(II), adsorption capacityof5,7 mg g-1, the value of adsorption constant (K)1086,1 L mol-1 and the adsorption energy is 17,4 kJ mol-1. In addition and desorption studies for both metal ions showed that the desorption with sodium-EDTA has the largest percentage of desorption compared to HNO3, KNO3 and aquabidest.

Kata Kunci : Nanofiber PVA/kitosan/iota-karaginan, isoterm Langmuir, adsorpsi, desorpsi, Pb(II) dan Cu(II),Nanofiber polyvinyl alcohol/chitosan/iota-carrageenan, Langmuir isotherm, adsorption, desorption, Pb(II) and Cu(II)