PENGARUH POSISI GUGUS HIDROKSI SENYAWA TURUNAN ASAM BENZOAT TERHADAP PEMBENTUKAN NANOPARTIKEL PERAK DARI AgNO3

MAGHFIROH, Prof. Dr. Sri Juari Santosa, M.Eng. ; Dr. Suyanta, M.Si.

2015 | Tesis | S2 Ilmu Kimia

Telah dilakukan penelitian terkait karakter fisik nanopartikel perak yang terbentuk dari hasil reaksi antara prekursor AgNO3 dengan reduktor asam orto hidroksibenzoat, asam para hidroksibenzoat dan asam galat. Penelitian ini bertujuan untuk mengetahui pengaruh posisi gugus hidroksi pada beberapa senyawa turunan asam benzoat terhadap morfologi, ukuran, distribusi ukuran, dan stabilitas nanopartikel perak yang dihasilkan. Sintesis nanopartikel perak dilakukan menggunakan metode reduksi kimia dengan variasi jenis reduktor, konsentrasi reduktor, konsentrasi prekursor dan pH sistem. Potensial reduksi senyawa reduktor dikarakterisasi dengan metode voltametri siklik menggunakan electrochemical analyzer, Surface Plasmon Resonance (SPR) koloid nanopartikel perak menggunakan spektrofotometer UV-Vis, morfologi nanopartikel perak menggunakan Transmission Electron Microscope, sedangkan ukuran dan distribusi ukuran nanopartikel perak dihitung menggunakan program ImageJ versi 1.48. Hasil penelitian menunjukkan bahwa nilai potensial reduksi dari asam orto hidroksibenzoat sebesar -0,4390 V, asam para hidroksibenzoat sebesar -0,5037 V, dan asam galat sebesar -0,4951 V. Nanopartikel perak terbentuk pada pH basa untuk semua jenis reduktor. Sensitivitas reduktor diselidiki dengan melakukan sintesis nanopartikel perak pada berbagai variasi konsentrasi AgNO3 dan didapat nilai batas deteksi dari asam orto hidroksibenzoat, asam para hidroksibenzoat dan asam galat masing-masing sebesar 5,10��10-6 mol L-1, 1,24��10-6 mol L-1, dan 2,58��10-5 mol L-1. Berdasarkan hasil analisis TEM diketahui bahwa ukuran nanopartikel perak yang dihasilkan oleh asam orto hidroksibenzoat sebesar 93,65�±35,45 nm, asam para hidroksibenzoat sebesar 60,83�±16,99 nm, dan asam galat sebesar 60,41�±15,69 nm. Koloid nanopartikel perak disimpan dalam ruang terbuka pada suhu kamar selama 6 minggu untuk melihat stabilitas nanopartikel perak. Nanopartikel perak yang paling stabil adalah nanopartikel perak yang disintesis dengan asam para hidroksibenzoat, disusul oleh yang disintesis dengan asam galat dan yang disintesis dengan asam orto hidroksibenzoat.

Physical character of the silver nanoparticles synthesized by AgNO3 as precursor and ortho hydroxybenzoic acid, para hydroxybenzoic acid and gallic acid as reducing agents was investigated. The aim of this study was to determine the effect of the hydroxyl group position on some derivative compounds of benzoic acid toward the morphology, size, size distribution and stability of the resulting silver nanoparticles. Synthesis of silver nanoparticles was performed using chemical reduction method with variations in the type reducing agents, reducing agents concentration, precursor concentration and pH of the system. The reduction potential of reducing agents was characterized by cyclic voltammetry method using electrochemical analyzer, the Surface Plasmon Resonance (SPR) of colloidal silver nanoparticles using UV-Vis spectrophotometer, the morphology of silver nanoparticles using Transmission Electron Microscope (TEM), while the size and size distribution of silver nanoparticles was calculated using ImageJ program version 1.48. The results showed that the potential reduction of ortho hydroxybenzoic acid, para hydroxybenzoic acid, and gallic acid was -0.4390 V, -0.5037 V, and -0.4951 V, respectively. In the formation of colloidal silver nanoparticles, an alkaline system was required for all types of reducing agent. Sensitivity reducing agents was investigated by synthesis of silver nanoparticles at various concentrations of AgNO3. Limit of detection of ortho hydroxybenzoic acid, para hydroxybenzoic acid, and gallic acid were 5.10��10-6 mol L-1, 1.24��10-6 mol L-1, dan 2.58��10-5 mol L-1, respectively. Based on TEM analysed it was known that the size of the silver nanoparticles produced by ortho hydroxybenzoic acid, para hydroxybenzoic acid and gallic acid was 93.65 �± 35.45 nm, 60.83 �± 16.99 nm, and 60.41 �± 15.69 nm, respectively. Colloidal silver nanoparticles was stored in the open space at room temperature for 6 weeks in order to investigate the stability of silver nanoparticles. The most stable of silver nanoparticles was that synthesized by para hydroxybenzoic acid, followed by that synthesized by gallic acid and that synthesized by ortho hydroxybenzoic acid.

Kata Kunci : nanopartikel perak, gugus hidroksi, asam orto hidroksibenzoat, asam para hidroksibenzoat, asam galat /silver nanoparticles, hydroxil group, ortho hydroxybenzoic acid, para hydroxybenzoic acid, gallic acid