KAJIAN IMMOBILISASI LOGAM BERAT PADA LUMPUR IPAL SEWON DAN POTENSI PEMANFAATANNYA SEBAGAI MATERIAL BANGUNAN

AGUNG TRIYONO, Ir. Suprapto Siswosukarto, Ph.D.;A. Tawfiequrrahman Y. ST. MT. D.Eng

2015 | Tesis | S2 Teknik Sipil

Lumpur pada Instalasi Pengolahan Air Limbah (IPAL) Sewon mengandung logam berat yang bersifat reaktif, korosif dan beracun. Jika konsentrasinya melebihi baku mutu maka diperlukan penanganan lebih lanjut. Untuk meminimalisasi dampak yang ditimbulkan oleh logam berat pada lumpur IPAL Sewon, maka dilakukan penelitian untuk mengkaji proses immobilisasi logam berat pada lumpur IPAL Sewon agar tidak mencemari lingkungan. Media padat sebagai produk dari proses immobilisasi diharapkan dapat dimanfaatkan sebagai material bangunan berupa paving blok dan atau batako. Dalam proses immobilisasi logam berat ini, agregat pasir disubstitusi dengan lumpur IPAL Sewon. Variasi substitusi lumpur IPAL adalah 0%; 2,5%; 5%; 7,5%; 10%; 20%; 30% dan 40%. Bahan semen, pasir, lumpur IPAL dan air dicampur kemudian dicetak berbentuk kubus dengan dimensi 6 cm x 6 cm x 6 cm. Setelah benda uji berumur 28 hari dilakukan uji Toxicity Characteristic Leaching Procedure (TCLP) untuk parameter logam berat Pb, Cu dan Zn. Selanjutnya dilakukan uji kuat tekan, keausan dan penyerapan air. Hasil penelitian menunjukkan bahwa immobilisasi logam berat dengan paving blok dan batako yang dibentuk dengan substitusi lumpur IPAL Sewon berpotensi untuk mengurangi mobilitas logam berat yang terkandung dalam lumpur IPAL Sewon dengan konsentrasi logam berat Pb, Cu dan Zn yang terlepas masih berada di bawah baku mutu yang ditetapkan. Kadar substitusi lumpur IPAL yang potensial untuk mendapatkan paving blok dengan nilai kuat tekan dan penyerapan air yang memenuhi persyaratan adalah 2,5% - 10%. Kadar substitusi lumpur yang potensial untuk mendapatkan paving blok dengan nilai keausan yang memenuhi persyaratan adalah 2,5%. Sedangkan kadar substitusi lumpur yang potensial untuk mendapatkan batako dengan kuat tekan dan penyerapan air yang memenuhi persyaratan adalah 2,5% - 40%. Lumpur IPAL Sewon yang dihasilkan dalam satu periode penyedotan (6 bulan) jika dibuat menjadi paving blok mutu C (untuk pejalan kaki) dengan tebal 6 cm dan batako kualitas I dengan tebal 10 cm maka diperoleh paving blok dengan luas 44.367 m2 dan batako dengan luas 26.620 m2.

Sludge in the Waste Water Treatment Plant (WWTP) Sewon contains heavy metals that are reactive, corrosive and toxic. If its concentrations exceed the quality standards, it would require further treatments. To minimize the impact of the heavy metals in the WWTP Sewon's sludge, then a study to assess the process of immobilization of the heavy metals in the WWTP Sewon's sludge needs to be carried out in order not to pollute the environment. A solid medium as a product of the immobilization process were expected to be used as building materials in the form of paving blocks or concrete blocks. In the process of immobilization of the heavy metals, the sand agregate was substituted with the WWTP Sewon's sludge. The variations of the substitution of the WWTP's sludge were 0%; 2.5%; 5%;7.5%; 10%; 20%; 30% and 40%. Cement, sand, WWTP's sludge and water were mixed then formed cuboid with dimensions of 6 cm x 6 cm x 6 cm. After the test objects reached 28 days, Toxicity Characteristic Leaching Procedure (TCLP) for parameters of heavy metals Pb, Cu and Zn was then tested. Further, compressive strength, wear and moisture absorption were also tested. The results showed that the immobilization of the heavy metals using paving blocks and concrete blocks formed by the substitution of the WWTP Sewon's sludge was potential to reduce the mobility of the heavy metals contained in the WWTP Sewon's sludge with the concentrations of the heavy metals Pb, Cu and Zn detached still below the quality standards established, the substitution levels of the WWTP's sludge potential to obtain paving blocks with the compressive strength and the moisture absorption meeting the requirements were 2.5% - 10%. The substitution level of the sludge potential to obtain paving blocks with the wear values that met the requirements was 2.5%. While the substitution levels of the sludge potential to obtain compressive strength and water absorption meeting the requirements were 2.5% - 40%. The WWTP Sewon's sludge generated in one period of suction (6 months) if made into quality C paving blocks (for pedestrians) with a 6 cm thick and quality I concrete blocks with a thickness of 10 cm were paving blocks with an area of 44,367 m2 and concrete blocks with an area of 26,620 m2.

Kata Kunci : Lumpur IPAL Sewon,immobilisasi,Paving blok,Batako