PEMBUATAN MEMBRAN N-DODESIL KITOSAN DENGAN TEKNIK PHASE INVERSION (PI) DAN MOLECULAR IMPRINTING POLYMER (MIP) SERTA APLIKASINYA UNTUK TRANSPOR UREA

DWI HERMAYANTININGSIH, Dr. Dwi Siswanta, M.Eng.

2015 | Tesis | S2 Ilmu Kimia

Penelitian tentang transpor urea menggunakan membran kitosan, N-dodesil kitosan dan paduannya telah dilakukan. N-dodesil kitosan disintesis secara alkilasi dengan mereaksikan kitosan dan n-dodesil bromida. Membran dibuat dengan phase inversion (PI) dan molecular imprinting polymer (MIP). Prinsip teknik phase inversion yaitu mengubah bentuk polimer dari fasa cair menjadi fasa padatan, sedangkan teknik molecular imprinting polymer yaitu mencetakkan sejumlah molekul ke dalam membran. Transpor urea dilakukan dengan menggunakan chamber berisi membran kitosan, N-dodesil kitosan serta paduannya yang memisahkan antara fasa sumber dengan fasa akseptor. Variabel dalam penelitian ini adalah konsentrasi urea sebagai fasa sumber, teknik pembuatan membran dan komposisi membran. Transpor menggunakan 50 mL larutan urea 1000, 1500 dan 2000 ppm sebagai fasa sumber dan 50 mL akuabides sebagai fasa akseptor, kedua fasa diatur pada pH 7,4. Konsentrasi urea setelah transpor pada fasa sumber dan akseptor diukur menggunakan 4- dimetilamino benzaldehida menggunakan spektrofotometer UV-Vis pada panjang gelombang 432 nm. Hasil karakterisasi dengan FT-IR menunjukkan keberhasilan alkilasi yaitu hilangnya serapan vibrasi bengkok amina primer (-NH2), munculnya serapan vibrasi ulur C-H alifatik dari gugus dodesil. Hasil karakterisasi menggunakan SEM menunjukkan bahwa morfologi membran molecular imprinting polymer tampak lebih halus dan merata dibandingkan membran inversi fasa. Nilai fluks rata-rata tertinggi dihasilkan oleh membran paduan molecular imprinting polymer yaitu sebesar 9,69 × 10-3 g/m2s, sedangkan nilai fluks rata-rata terendah dihasilkan oleh membran paduan inversi fasa yaitu sebesar 6,40 × 10-3 g/m2s. Kata kunci: membran, N-dodesil kitosan, transpor dan urea

A study on urea transport trough membranes based on chitosan and N-dodecyl chitosan and its blend had been conducted. N-dodecyl chitosan was synthesized by alkylation between chitosan and n-dodecyl bromide. Membranenes were prepared by phase inversion (PI) and molecular imprinting polymer (MIP) techniques. Principle of phase inversion technique is change liquid phase to solid phase, while molecular imprinting polymer technique is templating molecules into membrane. The urea transport was prepared with chitosan, N-dodecyl chitosan and its blend membrane using chamber, membrane separates the source and acceptor phase. Variable in this research was the concentration of urea as source phase, technique of membrane preparation and the composition of membrane. The source phase were prepared 50 mL of urea 1000, 1500 and 2000 ppm and acceptor phase 50 mL of bisdestilled water, both of phase adjusted to pH 7.4. The concentration of urea after transport in the source and acceptor phase was determined using 4-dimethylamino benzaldehyde using UV-Vis spectrophotometer at λ 432 nm. The results of FTIR showed the success of the alkylation that is marked by the loss of bending vibration absorption of primary amines (-NH2) and appearance of aliphatic C-H stretching vibration absorption of dodecyl groups. The morphology of the molecular imprinting polymer membranes appears more smoother and solid than phase inversion. Molecular imprinting polymer blending membrane is the highest average flux 9.69 × 10-3 g/m2s, while the lowest absorption was phase inversion blending membrane at 6.40 × 10-3 g/m2s. Keywords: membrane, N-dodecyl chitosan, transport and urea

Kata Kunci : membran, N-dodesil kitosan, transpor dan urea; membrane, N-dodecyl chitosan, transport and urea