PENGARUH PENUAAN TERHADAP DENSITAS IKATAN SILANG RESIN KOMPOSIT PACKABLE BULK-FILL, SONIC ACTIVATED BULK-FILL DAN PACKABLE KONVENSIONAL
MARGARETA RINASTITI, drg. Diatri Nari Ratih, M.Kes Sp.KG., Ph.D.
2015 | Tesis | SP ILMU KONSERVASI GIGIResin komposit telah banyak digunakan karena bersifat adhesif serta mempunyai sifat estetik, fisiko-kimia yang baik. Keadaan rongga mulut yang dinamis dapat menyebabkan terjadinya penuaan berupa degradasi resin komposit yang Selain itu, keausan dan pengkerutan polimerisasi dapat menurunkan ketahanan resin komposit. Secara klinis keadaan tersebut mengakibatkan diskolorasi, fraktur, delaminasi, chipping dan kegagalan adhesi pada tepi restorasi, kebocoran mikro , sensitivitas dentin dan karies sekunder. Resin komposit bulk-fill dikembangkan untuk meminimalisasi sifat-sifat negatif tersebut. Salah satu indikator yang digunakan untuk memprediksi ketahanan resin komposit terhadap penuaan dan wear adalah densitas ikatan silang yang dapat diukur dengan tes softening. Tujuan dari penelitian ini adalah untuk mengevaluasi densitas ikatan silang resin komposit packable bulk-fill, resin komposit sonic activated bulk-fill dan resin komposit packable konvensional sebelum dan sesudah proses penuaan. Penelitian ini menggunakan tiga jenis resin komposit, yaitu resin komposit packable bulk-fill, sonic activated bulk-fill dan packable konvensional. Dua puluh spesimen dari masing-masing jenis resin komposit (N=60) berbentuk silinder dengan diameter 5mm dan tinggi 4mm diukur kekerasannya menggunakan alat pengukur kekerasan mikro Vicker’s, hasilnya dicatat sebagai VHN1. Selanjutnya dua puluh specimen tersebut dibagi menjadi dua kelompok, sepuluh spesimen direndam dalam etanol absolute selama 24 jam dan sepuluh specimen direndam dalam akua destilata selama 30 hari. Setelah perendaman, diukur kekerasannya. Angka kekerasan setelah perendaman dalam etanol absolut dicatat sebagai VHN2 dan dalam akua destilata dicatat sebagai VHN3. Densitas ikatan silang didapatkan dengan cara mengurangi nilai kekerasan setelah perendaman dan sebelum perendaman. Analisis statistika ANAVA dua jalur membuktikan bahwa terdapat perbedaan yang bermakna (p < 0,05) pada densitas ikatan silang antara ketiga jenis resin komposit serta perendaman dalam akua destilata dan etanol absolut. Hasil uji Tukey menunjukkan terdapat perbedaan diantara semua kelompok resin komposit dan kelompok perlakuan, kecuali antara resin komposit sonic activated bulk-fill dan resin komposit packable konvensional, yang direndam dalam etanol absolut selama 24 jam. Kesimpulan dari penelitian ini adalah densitas ikatan silang resin komposit packable bulk-fill, sonic activated bulk-fill dan packable konvensional setelah proses penuaan lebih tinggi dibandingkan dengan sebelum proses penuaan. Setelah proses penuaan, densitas ikatan silang resin komposit sonic activated bulk-fill lebih tinggi dibandingkan dengan resin komposit packable bulk-fill, dan resin komposit packable konvensional mempunyai densitas ikatan silang yang paling rendah. Kata kunci : resin komposit, bulk-fill, packable, sonic activated, densitas ikatan silang, penuaan.
Composite resin has been widely used in dentistry due to its advantage properties. The aging process of composite under oral environment result in some failures such as discoloration, degradation, microleakage, wear, ditching at the margins, delamination or simply fracture and/or chipping being often experienced in clinical situations. Furthermore, wear and polymerizations shrinkage remains the problems that affect the clinical success of the dental composite such as microleakage, resuting dentin sensitivity and secondary caries.Lately, Lately a bulk-fill resin composite has been developed to eliminate the disadvantage of resin composite and enhance the longevity of restoration. Cross link density is one of the indicators to evaluate the resistance of resin composite to aging and wear. Cross link density of a polymer network can be assessed by softening test. The aims of this research was to evaluate the cross link density of packable bulk-fill, sonic activated bulk-fill and packable conventional resin composites prior to- and after aging. Packable bulk-fill, sonic activated bulk-fill and packable conventional resin composites were used in this study. Twenty disc shaped specimens (N = 60) were fabricated by placing unpolymerized composite resins into cylindrical cavities ( :5 mm, height : 4 mm). The Vickers hardness number (VHN) was determined using a microhardness tester. The results were signed as VHN1. Afterward, a half of the specimens were immersed in ethanol absolute for 24 hours and a half in destilation water for 30 days and post conditioning hardness (VHN2 and VHN3) were determined. . Hardnessdeterioration was computed as follows: ΔVHN = VHN1 – VHN 2 and VHN1 – VHN3. All crosslink density data were then subjected to two-way ANOVA/Tukey’s post hoc test at a significance level of 0.05 to determine differences in crosslink density between the various resin composites and aging condition. Type of composite resins and surface conditioning methods both showed significant effect on the results. Tukey’s post hoc test showed the differences among all group except between sonic activated bulk-fill dan konvensional packable resin composites after immersion in ethanol absolute. With the limitation of the current study, it can be concluded that there is significant effect of resin composite types and aging on crosslink density. The aging process was increased crosslink density of packable bulk-fill, sonic activated bulk-fill and packable conventional resin composites. Sonic activated bulk-fill resin composite revealed the highest cross link density after aging process, followed by packable bulk-fill packable conventional resin composites. Keywords: composite resin, packable bulk-fill, sonic activated bulk-fill, packable conventional, crosslink density, aging
Kata Kunci : resin komposit, bulk-fill, packable, sonic activated, densitas ikatan silang, penuaan; composite resin, packable bulk-fill, sonic activated bulk-fill, packable conventional, crosslink density, aging