PENGARUH PENGGUNAAN BAHAN IRIGASI NaOCl DAN KOMBINASINYA TERHADAP KEKUATAN GESER PELEKATAN RESIN KOMPOSIT PADA DENTIN MENGGUNAKAN BONDING SELF ETCH

WENY SETYANINGSIH, drg. Ema Mulyawati, M.S., Sp.KG (K).

2015 | Tesis | SP ILMU KONSERVASI GIGI

Bahan irigasi saluran akar yang digunakan selama prosedur preparasi biomekanik juga berkontak dengan dinding dentin mahkota gigi yang kemungkinan dapat mengubah komposisi dentin mahkota yang selanjutnya berinteraksi dengan bahan restorasi. Tujuan penelitian ini adalah untuk mengetahui pengaruh bahan irigasi NaOCl dan kombinasinya terhadap kekuatan geser pelekatan resin komposit pada dentin menggunakan bonding self etch. Lima belas gigi premolar maksila dipotong dengan pemotong berbentuk diskus secara longitudinal arah mesiodistal sampai area CEJ. Kelompok I (n=5) diirigasi dengan NaOCl 2,5%, kelompok II (n=5) diirigasi dengan NaOCl 2,5% dan EDTA 17%, sedangkan kelompok III(n=5) diirigasi dengan NaOCl 2,5%, EDTA 17%, dan klorheksidin diglukonat 2%. Setelah diirigasi, gigi dipotong pada area CEJ dengan arah transversal sehingga dari satu gigi diidapatkan dua spesimen yang kemudian ditanam di blok akrilik. Selanjutnya dilakukan penumpatan resin komposit menggunakan bonding self etch generasi ke-7 (G bond, GC). Setelah dilakukan inkubasi selama 24 jam pada suhu 37oC dan thermocycling sebanyak 25 kali kemudian dilakukan uji geser menggunakan Universal Testing Machine (Zwick, USA). Data yang diperoleh diuji dengan anava satu jalur dan uji LSD. Hasil penelitian menunjukkan bahwa terdapat perbedaan bermakna kekuatan geser pelekatan resin komposit pada dentin antara kelompok I dengan kelompok III dan antara kelompok II dengan kelompok III, sedangkan antara kelompok I dan II perbedaanya tidak signifikan. Kelompok III memiliki kekuatan geser pelekatan paling rendah dibandingkan kelompok I dan II. Pada penelitian ini disimpulkan bahwa terdapat pengaruh penggunaan larutan irigasi NaOCl dan kombinasinya terhadap kekuatan geser pelekatan resin komposit pada dentin menggunakan bonding generasi 7. Selain itu, disimpulkan juga bahwa tidak terdapat perbedaan kekuatan geser pelekatan antara kelompok yang diirigasi dengan NaOCl 2,5% dan kelompok yang diirigasi dengan kombinasi NaOCl 2,5% dan EDTA 17%. Kelompok yang diirigasi dengan kombinasi NaOCl 2,5%, EDTA 17% dan khlorheksidin diglukonat 2% menunjukkan kekuatan geser pelekatan yang paling rendah. Kata kunci: NaOCl, EDTA, klorheksidin diglukonat, bonding self etch, kekuatan geser, resin komposit.

The root canal irrigant used during cleaning and shaping of the root canal system might contact with the coronal dentin and change its chemical composition. Those coronal dentin would interact with the coronal restoration. The aim of this research was to investigate the influence root canal irrigant especially sodium hypochlorite (NaOCl) and its combination on shear bond strength of the resin composite restoration to dentin using one-step self-etch adhesive system. Fifteen maxillary premolar were sectioned longitudinally (mesiodistal direction) until reach the CEJ area. The subjects were divided into 3 groups: The first group (n=5) were irrigated with 2,5% NaOCl, the second group (n=5) were irrigated with 2,5% NaOCl and 17% EDTA, the third group (n=5) were irrigated with 2,5% NaOCl, 17% EDTA and 2% chlorhexidine digluconate. After the irrigation protocol, the teeth were sectioned transversally in the CEJ area to obtain 2 specimens from each tooth. In addition the specimens were fixed in the acrylic block and then restored with composite resin using 7th generation adhesive system/one-step self-etch adhesive system (G Bond,GC). The specimens were incubated for 24 hours at 37o C then the thermocycling was carried out (25 times). The shear bond strength measurement was carried out using Universal Testing Machine (Zwick, USA). The data were statistically analyzed using one way anava and LSD. The results showed that the shear bond strength between the first group and third group, and between the second group and third group were significantly different, while between the first group and the second group were not different significantly.The third group has the lowest shear bond strength among the other groups. The conclusion were there was influence of NaOCl and its combination on the shear bond strength of resin composite restoration to dentin using 7th generation adhesive system. There was no diffference on shear bond strength between the group that was irrigated with 2,5% NaOCl alone and the group that was irrigated with 2% NaOCl and 17% EDTA. The group that was irrigated with 2,5%, NaOCl, 17% EDTA and 2% chlorhexidine digluconate has the lowest shear bond strength among the other groups. Keywords: NaOCl, EDTA, chlorhexidine digluconate, self-etch adhesive system, shear bond strength, resin composite

Kata Kunci : NaOCl, EDTA, klorheksidin diglukonat, bonding self etch, kekuatan geser, resin komposit