Studi Polyethylene Terephtalate dengan Aditif Styrene-Butadiene Rubber sebagai Matriks Immobilisasi Strontium Klorida Hexahidrat

PRASETYO HARYO SADEWO, Ir. Susetyo Hario Putero, M.Eng.; Ir. Nunung Prabaningrum, M.T.,Ph.D

2015 | Skripsi | S1 TEKNIK NUKLIR

Telah dilakukan penelitian tentang immobilisasi limbah strontium dengan daur ulang plastik polietilen terephtalat (PET). Sifat-sifat PET sebagai matriks telah ditentukan melalui pengujian kadar air bebas, laju pelindian, dan flashpoint. Penelitian dilakukan dengan limbah simulasi 88SrCl2.6 H20 yang dijerap dengan menggunakan zeolit alam sebanyak 30wt.% dicampur dengan polietilen terephtalat yang telah dilelehkan. Styrene Butadiene Rubber (SBR) digunakan sebagai aditif dengan kandungan SBR sebesar 0, 20, 40 wt.%. Kadar air bebas ditentukan dengan memanaskan sampel di dalam oven pada temperatur 110oC selama 45 menit. Pengujian laju pelindian dilakukan dengan merendam blok limbah dalam air tanah selama 21 hari. Strontium yang terlindi dianalisis dengan atomic absorption spectrometer. Pengujian flashpoint dilakukan dengan menggunakan metode Cleveland Open Cup. Sifat-sifat PET sebagai blok limbah melalui pengujian kadar air bebas, laju pelindian dan flashpoint adalah seluruh blok limbah untuk semua kandungan aditif memiliki kadar air bebas antara 0,40 hingga 0,99 %; laju pelindian hari ke-21 untuk kandungan aditif 0, 20, 40% berturut-turut sebesar 1,24x10-7, 6,51x10-7, dan 2,74x10-7 g.cm-2.hari-1. Ketahanan termal dari blok limbah untuk kandungan aditif 0, 20, 40% berturut-turut adalah 280oC (flashpoint), 320oC (firepoint), dan 270oC (firepoint).

This research was conducted to determine properties and feasibility of Polyethylene Terephtalate (PET) as a matrix for immobilizing nuclear waste. Properties included are free water content, leaching rate, and flashpoint. Nuclear waste was simulated by 88SrCl2.6 H20 which has been adsorbed with natural zeolite. This zeolite loaded by 30wt.% of 88SrCl2.6 H20 and was mixed with melted polyethylene terephtalate. Styrene Butadiene Rubber was used as an additive at 0, 20, 40 wt.%. The waste concentration was set at 30 wt.%. Free water content was determined by heating the sample using an oven at 110oC for 45 minutes. The leaching rate was determined by soaking the block in groundwater for 21 days. The strontium leached into the water was analyzed using an atomic absorption spectrometer. The flashpoint was tested by Cleveland Open Cup method. The properties of PET as a matrix of nuclear waste immobilization are: the free water content of all the blocks regardless of the additive percentage are between 0,40 to 0,99 %; leaching rate on the 21st day for each additive percentage of 0, 20, 40% were 1.24x10-7, 6.51x10-7, and 2.74x10-7 g.cm-2.day-1 respectively. The thermal strength of the blocks for each additive percentage of 0, 20, 40% are respectively 280oC (flashpoint), 320oC (firepoint), and 270oC (firepoint).

Kata Kunci : imobilisasi, polietilen terephtalat, limbah radioaktif, limbah plastik