PENGARUH SUHU KALSINASI, MASSA LIGNIN DAN KONSENTRASI Ti (IV) TERHADAP FOTOAKTIVITAS KATALITIK TiO2-LIGNIN PADA FOTOREDUKSI ION Hg(II)

FIBY ACHMAD V., Prof. Dr. Endang Tri Wahyuni, M.S.; Dr.rer.nat. Nurul Hidayat Aprilita, M.Si.

2015 | Skripsi | S1 KIMIA

Telah dilakukan uji pengaruh suhu kalsinasi, masa lignin dan konsentrasi Ti (IV) terhadap fotoaktivitas katalitik TiO2-lignin pada reaksi fotoreduksi ion Hg(II). Komposit TiO2-lignin diperoleh dengan mengaduk 50 mL larutan titanium tetraisopropoksida (TTIP)/methanol dengan lignin selama 24 jam. Pengaruh konsentrasi TTIP dipelajari dengan memvariasi konsentrasinya antara 0,1; 0,3; 0,5; 1,0; dan 1,5M terhadap suhu kalsinasi dan massa lignin yang konstan yaitu 200 derajad Celcius dan 250 mg. Uji pengaruh massa lignin dilaksanakan dengan memvariasi massanya antara 100, 250, dan 500 mg terhadap konsentrasi TTIP dan suhu kalsinasi yang konstan yaitu 0,5 M dan 200 derajad Celcius. Sedangkan untuk mempelajari pengaruh suhu kalsinasi dilakukan dengan mereaksikan larutan TTIP 0,5 M dengan 250 mg lignin kemudian dikalsinasi pada suhu yang bervariasi yaitu 100; 300; dan 500 derajad Celcius. Komposit yang diperoleh kemudian diuji aktivitas fotokatalitknya terhdap ion Hg(II), diamati kristalinitas dengan difraktometersinar-X (XRD 6000X Shimadzu), kadar TiO2-nya secara gravimetrik dan ukuran partikel TiO2 dengan Transmision Electron Microscope (TEM) JEM 1400. Hasil pengamatan foto TEM menunjukkan bahwa pengembanan TiO2 pada lignin akan menyebabkan penurunan ukuran partikelnya dari 110-120 nm menjadi 8,25-11,91 nm (nano partikel). Kenaikan suhu kalsinasi dari 100 derajad Celcius hingga 500 derajad Celcius meningkatkan kristalinitas TiO2 pada TiO2-lignin. Fotoreduksi terhadap 50 mL larutan Hg(II) 10 ppm oleh fotokatalis TiO2-lignin mencapai maksimum pada suhu kalsinasi 500 derajad Celcius, massa lignin 250 mg, dan konsentrasi TTIP 1 M.

The study on the effect of calcination temperature, lignin mass and Ti (IV) concentration on photocatalytic activity of TiO2-lignin on photoreduction of Hg (II) ion has been conducted. Photocatalyst of TiO2-lignin was prepared by impregnating 50 mL of titanium tetraisopropoxide (TTIP)-methanol solution into lignin for 24 hours and followed by calcination process. The effect of TTIP concentration was studied by varying the concentration of 0.1, 0.3, 0.5, 1.0, and 1.5 M in the constant calcination temperature and lignin mass as much as 200 Celcius degree and 250 mg. The effect of lignin mass was studied by varying the mass i.e. 100, 250, and 500 mg in the constant TTIP concentration and calcination temperature, 0.5 M and 200 Celcius degree . While to study the effect of calcination temperature, TTIP solution 0.5 M was reacted with 250 mg lignin followed by calcination process in various temperature, 100, 300, and 500 Celcius degree. The TiO2-lignin was examined as photocatalyst for Hg (II) ion photoreduction, and the cristalinity was observed by X ray-diffractometer (XRD 6000X Shimadzu), the TiO2 amount wa determined by gravimetric and the size of TiO2 particles was identified by Transmission Electron Microscope (TEM) JEM 1400. The research result from TEM photos indicate that the impregnation of TiO2 on lignin can decrease the particles size from 110-120 nm to 8.25-11.91 nm (nano particle). The incrase of calcination temperature from 100 Celcius degree until 500 Celcius degree incrases the cristalinity of TiO2 on TiO2-lignin. The photoreduction of 50 mL Hg (II) 10 ppm solution by photocatalytic TiO2-lignin reaches maximum (85.25 %) by using TiO2-lignin calcinated at 500 Celcius degree, with lignin mass of 250 mg, and TTIP concentration of 1 M.

Kata Kunci : TiO2-lignin, nanopartikel, fotokatalitik, reduksi Hg(II)