AKTIVASI ABU LAYANG AMPAS TEBU MENGGUNAKAN HIDROGEN PEROKSIDA (H2O2) DAN PEMANFAATAANNYA SEBAGAI ADSORBEN ZAT WARNA INDIGOSOL YELLOW IGK PADA LIMBAH HOME INDUSTRY BATIK

HEVIA ANGGUN VIBRIARTI, Prof. Dr. Sri Juari Santosa M.Eng ; Prof. Dr. Narsito

2014 | Skripsi | S1 KIMIA

Aktivasi abu layang ampas tebu menggunakan hidrogen peroksida (H2O2) dan pemanfaatannya sebagai adsorben zat warna indigosol yellow IGK pada limbah home industry batik telah dilakukan. Aktivasi melalui proses pencucian abu layang ampas tebu dengan campuran larutan HCl 0,1 M dan HF 0,3 M kemudian diaktivasi menggunakan larutan H2O2 pada variasi konsentrasi (0,5,1,2,dan5M). Spektroskopi Inframerah (FT-IR) dan difraksi sinar X (XRD) digunakan untuk mengkarakterisasi abu layang ampas tebu sebelum dan setelah aktivasi. Selain itu, luas permukaan spesifik dan volume pori juga ditinjau. Adsorpsi zat warna indigosol yellow IGK yang telah diaktivasi dipelajari dengan melihat efek keasaman, waktu kontak dan konsentrasi zat warna. Hasil menunjukkan bahwa abu layang ampas tebu pada dasarnya bersifat amorf tetapi mengandung kristal SiO2. Aktivasi menggunakan H2O2 meningkatkan kristalinitas dari SiO2 dan memperbesar luas permukaan dan volume pori. Adsorpsi zat warna indigosol yellow IGK mempunyai pH optimum 4,0, waktu kontak 60 menit dan konsentrasi zat warna sebesar 100 mg/L untuk setiap 25 mg adsorben. Adsorpsi mengikuti model kinetika pseudo orde dua dengan konstanta laju pseudo orde dua sebesar 0,003 g/mg.menit Adsorpsi mengikuti model isoterm Langmuir dengan nilai kapasitas adsorpsi sebesar 5,18 x 10-3 mol/g dan energi adsorpsi sebesar 30,52 kJ/mol

Activation of baggase fly ash using hydrogen peroxide (H2O2) and utilization as an adsorbent for indigosol yellow IGK dye in wastewater of batik home industry has been done. The activation was proccesed by washing baggase fly ash with a mixed solution of 0.1 M HCl and 0.3 M HF and then followed by activation using H2O2 solution at various concentration (0.5,1,2 and 5 M). Infrared (FT-IR) spectroscopy and X-ray Difraction (XRD) have been used to characterized the baggase fly ash before and after activation. In addition, the surface area, pore volume and pore size were monitored. The adsorption of indigosol yellow IGK dye on the activated baggase fly ash was studied by examining the effect of initial medium acidity, contact time and concentraton of the dye. The results showed that baggase fly ash was basically amorphous but contained crystaline SiO2. Activation using H2O2 enhanced the crystalinity of SiO2 and enlarged the surface area and pore volume. The adsorption of indigosol yellow IGK dye was optimum at pH 4.0, contact time 60 minutes and concentration of the dye 100 mg/L for every 20 mg adsorbent. The adsorption followed the pseudo second-order kinetic model with pseudo second-order rate constant 0.003 g/mg.min The adsorption with Langmuir isotherm model with adsorption capacity 5.18x10-3 mol/g and adsorption energy 30.52 kJ/mol

Kata Kunci : abu layang ampas tebu, adsorpsi, indigosol yellow IGK, hidrogen peroksida, isoterm