PERBANDINGAN KEKUATAN GESER SERTA LETAK KEGAGALAN PELEKATAN BRAKET LOGAM DENGAN RESIN KOMPOSIT FLOWABLE ANTARA METODE ETCH AND RINSE DAN SELF ETCH

RULIYANTO, Drg. JCP. Heryumani S., MS., Sp.Ort (K)

2015 | Tesis | SP ORTODONSIA

Proses pelekatan braket melibatkan etsa email, aplikasi larutan primer dan resin komposit pada braket ortodontik. Perkembangan sistem pelekatan salah satunya adalah penyatuan bahan etsa dan primer ke dalam satu larutan yang disebut self etching primer. Proses pelekatan dengan larutan tersebut disebut metode self etch. Resin komposit yang digunakan pada pelekatan braket logam adalah resin komposit flowable. Tujuan penelitian ini adalah untuk membandingkan kekuatan geser serta letak kegagalan pelekatan braket logam dengan resin komposit flowable antara metode etch and rinse dan self etch. Penelitian dilakukan pada 30 gigi premolar pertama rahang atas yang dibagi menjadi 2 kelompok, yaitu kelompok 1 metode etch and rinse dan kelompok 2 metode self etch. Tiap sampel direkati braket dengan resin komposit flowable. Uji kekuatan geser dilakukan menggunakan mesin pengukur Universal Testing Machine. Uji Adhesive Remnant Index (ARI) digunakan untuk mengetahui letak kegagalan pelekatan braket menggunakan MacroX Microscope. Analisis statistik yang digunakan adalah Uji t dan Kolmogorov Smirnov. Hasil penelitian menunjukkan bahwa terdapat perbedaan kekuatan geser pelekatan braket logam dengan resin komposit flowable antara metode etch and rinse dan self etch. Nilai ARI kedua kelompok menunjukkan terdapat perbedaan lokasi kegagalan pelekatan braket ortodontik (p<0,05). Kesimpulan dari penelitian ini adalah kekuatan geser pelekatan braket logam dengan metode self etch lebih rendah dari pada metode etch and rinse, namun nilainya masih berada dalam rentang nilai kekuatan geser yang diperlukan, serta letak kegagalan perlekatan dengan metode etch and rinse terjadi antara bahan pelekat dengan mesh braket sedangkan metode self etch terjadi antara bahan pelekat dengan permukaan email. Kata kunci: Metode etch and rinse, self etch, resin komposit flowable, uji kekuatan geser, Adhesive Remnant Index (ARI)

The process of bracket attachment concists of etching email, application the primary solution to composite resin on orthodontic bracket. The development of attachment systems which is to unite etching and primary materials into a single solution that is called self- etching primer. The process of attachment bracket used this solution called self- etch method. Composite resin that used to attach metal bracket was flowable composite resin. The purpose of this study was to compare the shear bond strength and the failure of the metal bracket sticking with flowable composite resin between etch and rinse method and self-etch. The study was conducted on 30 maxillary first premolars were divided into 2 groups: group 1 ( etch and rinse method ) and group 2 ( self-etch method ). Each sample was then mounted bracket with flowable composite resin. Shear bond strength tests performed using Universal Testing Machine and Test Adhesive Remnant Index ( ARI ) was performed by a microscope MacroX. Statistical analyzes used were t-test and Kolmogorov Smirnov. The results showed a differences of shear bond strength between two group. ARI value of both group showed a differences for site of bond failure (p<0,05). The conclusion of this study is the shear bond strength of metal bracket with a self etch method is lower than etch-rinse methods, but its value is still within the range of shear bond strength values are required. Failure site with etch and rinse metode occurs between the adhesive and the bracket mesh while the self etch metode occurs between the surface of the enamel. Keywords : Etch and rinse Methode, self-etch, flowable composite resin, shear bond strength, Adhesive Remnant Index ( ARI )

Kata Kunci : Metode etch and rinse, self etch, resin komposit flowable, uji kekuatan geser, Adhesive Remnant Index (ARI)