STUDI PENURUNAN KADAR LOGAM Fe, Ni dan Cu PADA LIMBAH CAIR DENGAN SISTEM PEMISAH HIGH GRADIENT MAGNETIC SEPARATION (HGMS) MENGGUNAKAN ADSORBEN NANOPARTIKEL Fe3O4

DHAFID ETANA PUTRA, Dr. Edi Suharyadi M.Eng.

2015 | Tesis | S2 Ilmu Fisika

Telah dilakukan penelitian untuk menentukan tingkat efektivitas penyaringan limbah logam buatan Cu, Ni dan Fe dengan menggunakan High Gradient Magnetic Separation (HGMS). Penyaring elektromagnetik dibuat dari pipa Polyvinyl Chloride (PVC) berdiameter 1 inci yang diberi lilitan kawat berdiameter 0,45 mm, pipa kecil sebagai filter berdiameter 500 m dan terdiri dari 1173 lilitan. Penyaringan dilakukan dengan variasi medan magnet sebesar 2,3 Gs, 5,1 Gs dan 7,7 Gs. Pada penelitian ini diberikan 3 perlakuan dengan variasi arah medan magnet, yaitu medan magnet searah, berlawanan arah dan tegak lurus arah aliran sampel. Hasil penyaringan kemudian dianalisa kadar akhir logamnya dengan menggunakan Atomic Absorption Spectroscopy (AAS). Hasil penyaringan logam menunjukkan prosentase ion logam Cu (II) cenderung menurun, Ni (II) konstan dan Fe (II) naik. Logam Cu (II) pada arah medan magnet berlawanan arah aliran sampel sebesar 92,90%, 94,96%, 93,15% dan tegak lurus arah aliran sampel sebesar 96,58%, 94,71%, 95,67%. Logam Ni (II) pada arah medan magnet berlawanan arah aliran sampel sebesar 99,16%, 99,11%, 99,20% dan tegak lurus arah aliran sampel sebesar 99,32%, 99,38%, 99,30%. Logam Fe (II) secara maksimal pada arah medan magnet berlawanan arah aliran sampel sebesar 100%, 100%, 100% dan tegak lurus arah aliran sampel sebesar 100%, 100%, 100%. Hal ini terjadi karena Fe (II) termasuk bahan ferromagnetik yang memiliki momen magnetik spontan dan mempunyai elektron valensi yang banyak dibandingkan dengan Cu (II) dan Ni (II). Jadi, apabila diberi medan magnet maka Fe (II) spinnya akan cendrung mudah mensejajarkan dan mudah menempel pada pipapipa kecil HGMS. Kata-kata kunci : HGMS, limbah logam dan AAS

Research have been carried out to determine the effectiveness level of artificial metal s waste purification such as Cu, Ni and Fe using High Gradient Magnetic Separation (HGMS). Electromagnetic filter is made from Polyvinyl Chloride (PVC) pipe with 1-inch in diameter and coiled by wire (0,45 mm in diameter), small pipes as a filter with diameter of 500 m consist of 1173 coil. Purification is done by varying the magnetic field strength i.e 2,3 Gs, 5,1 Gs and 7,7 Gs. In this investigation, three treatments are given by changing the magnetic field direction, i.e the directions of the magnetic field is parallel, antiparallel and perpendicular respect to the sample flow. And then, purification samples were analyzed using Atomic Absorption Spectroscopy (AAS). The result showed that the percentage of Cu tends to decrease, Ni constant and Fe increase. Magnetic field with opposite direction to the sample flow, percentage of Cu ( II ) i.e 92.90 % , 94.96 % , 93.15 % and perpendicular to the sample flow i.e 96.58 % , 94.71 % , 95.67 %. Magnetic field with opposite direction to the sample flow, the percentage of Ni ( II ) i.e 99.16 % , 99.11 % , 99.20 % and perpendicular to the sample flow i.e 99.32 % , 99.38 % , 99.30 %. The percentage of Fe (II) maximally in the magnetic field with opposite to the sample flow i.e 100%, 100%, 100% and perpendicular to the sample flow i.e 100%, 100%, 100%. This result is caused by the Fe (II), a ferromagnetic material, which has a spontaneous magnetic moment and a little valence electrons paired compared to Cu (II) and Ni (II). So, when the magnetic field is applied to the artificial waste water, spin orientation in Fe (II) will easily tend to align and attach to small pipes in the HGMS system. Key words : HGMS, metals waste and AAS

Kata Kunci : HGMS, limbah logam dan AAS; HGMS, metals waste and AAS