PERBANDINGAN PENGARUH WAKTU PERENDAMAN DALAM SALIVA BUATAN TERHADAP PELEPASAN ION NIKEL DAN KROMIUM ANTARA KAWAT AUSTRALIA DENGAN KAWAT STAINLESS STEEL (Penelitian Laboratoris dengan Spektrofotometri Serapan Atom)

NOLISTA INDAH RASYID, Prof. DR. drg. Pinandi Sri Pudyani, SU., Sp.Ort (K)

2015 | Tesis | SP ORTODONSIA

Perawatan ortodontik cekat menggunakan beberapa macam kawat untuk menghasilkan kekuatan biomekanika yang sesuai dalam menggerakkan gigi. Teknik Begg menggunakan kawat Australia sedangkan pada teknik Edgewise menggunakan kawat stainless steel. Pemakaian kawat ortodontik didalam mulut dapat bereaksi dengan saliva menyebabkan terjadi pelepasan ion nikel dan kromium. Penelitian ini bertujuan untuk membandingkan pengaruh waktu perendaman dalam saliva buatan terhadap pelepasan ion nikel dan kromium antara kawat Australia tipe spesial dengan kawat stainless steel. Penelitian ini menggunakan 30 buah kawat Australia tipe spesial dan 30 buah kawat stainless steel dengan berat tiap kawat 0,12 gram. Kawat direndam selama 1, 7, 28, 35, 42, dan 49 hari didalam saliva buatan pH normal. Pemeriksaan pelepasan ion pada saliva menggunakan Spektrofotometri Serapan Atom. Analisis statistik menggunakan uji Kruskal-Wallis dengan signifikansi p<0,05. Hasil penelitian menunjukkan pelepasan ion nikel pada kawat Australia tipe spesial lebih besar dibandingkan dengan kawat stainless steel, terdapat perbedaan pelepasan jumlah ion nikel pada kawat Australia tipe spesial antara waktu perendaman dan terdapat interaksi antara jenis kawat dengan waktu perendaman. Ion nikel yang terlepas pada kawat Australia tipe spesial mulai terdeteksi pada hari ke-7 perendaman dan mencapai jumlah tertinggi pada hari ke- 35 sedangkan pada kawat stainless steel mulai terdeteksi pada perendaman hari ke-49. Pelepasan ion kromium pada kawat Australia tipe spesial dan kawat stainless steel tidak terdeteksi sampai perendaman hari ke-49. Kata kunci : Kawat Australia, stainless steel, waktu perendaman, ion nikel, ion kromium.

Orthodontic treatment uses several types of wire to produce biomechanical force to move teeth. Begg technique uses Australian wire, while Edgewise technique uses stainless steel wire. The orthodontic wire within the mouth interacts with saliva, causing the release of nickel and chromium ions. The objective of this study is to compare the effect of immersion time in artificial saliva between a special type of Australian wire and stainless steel on the release of nickel and chromium ions. This study used 30 Australian wires and 30 stainless steel wires, each of which weighed 0.12 grams. The wires were immersed for 1, 7, 28, 35, 42, and 49 days in artificial saliva with a normal pH. The release of ions in saliva was examined using Atomic Absorption Spectrophotometry. Meanwhile, statistical analysis employed the Kruskal-Wallis test with a significant p value <0.05. The results of research indicated that the release of nickel ions on the special type of Australian wire was larger than that on stainless steel wire; there were differences in the release of the amount of nickel ions on the special type of Australian wire in different immersion time; and there was a correlation between types of wire and immersion time. Nickel ions released from the special type of Australian wire were detected on the 7th day of immersion and reached its peak on the 35th day, while from stainless steel wire were detected on the 49th day of immersion. The release of chromium ions from the special type of Australian wire and stainless steel wire were not detected until the 49th day of immersion. Key words: Australian wire, stainless steel, immersion time, nickel ion, chromium ion

Kata Kunci : Kawat Australia, stainless steel, waktu perendaman, ion nikel, ion kromium; Australian wire, stainless steel, immersion time, nickel ion, chromium ion