Pengaruh Sn(II) dan Zn(II) Terhadap Kinetika Adsorpsi Au(III) oleh Asam Humat Tereterifikasi

RIAN KURNIAWAN, Prof. Dr. Triyono S.U.; Sri Sudiono, S.Si., M.Si.

2014 | Skripsi | KIMIA

Telah dilakukan isolasi, eterifikasi, dan karakterisasi asam humat serta studi mengenai pengaruh Sn(II) dan Zn(II) terhadap kinetika adsorpsi Au(III). Isolasi asam humat diawali dengan melarutkan tanah gambut, Rawa Pening ke dalam larutan NaOH 0,1 M di bawah atmosfer nitrogen, kemudian diendapkan dengan cara diasamkan menggunakan larutan HCl 0,1 M hingga pH = 2. Asam humat dimurnikan dengan cara dilarutkan ke dalam HCl 0,1 M : HF 0,3 M (1:1 v/v). Asam humat dieterifikasi menggunakan dimetilsulfat (DMS) dalam pelarut metanol-air. Dipelajari kinetika asam humat tereterifikasi dalam mengadsorpsi Au(III) serta pengaruh keberadaan Sn(II) dan Zn(II) di dalam sistem. Diamati konsentrasi Au(III) tiap waktu menggunakan AAS. Asam humat tereterifikasi baik yang sebelum maupun setelah interaksi dikarakterisasi menggunakan spektrofotometer FTIR, XRD dan foto mikroskop. Hasil yang diperoleh menunjukkan bahwa keberadaan ion Sn(II) dan Zn(II) di dalam sistem adsorpsi Au(III) oleh asam humat tereterifikasi akan menurunkan laju adsorpsinya. Konstanta laju adsorpsi (k) Au(III) tanpa logam lain, dengan adanya Sn(II), dan dengan adanya Zn(II) berturut-turut adalah 6,44 x 10^-4 mg.gram^-1.menit^-1; 2,79 x 10^-4 mg.gram^-1.menit^-1; dan 2,13 x 10^-4 mg.gram^-1.menit^-1.

It had been conducted the isolation, etherification, and characterization of humic acid and its study about the effects of Sn(II) and Zn(II) to adsorption of Au(III). The isolation of humic acid was begun by dissolving Pening swamp's peat soil into NaOH 0.1 M solution under nitrogen atmosphere, then percipitated by acidifying it using HCl 0.1 M solution until pH = 2. Humic acid was purified by dissolving it into HCl 0.1 M : HF 0.3 M (1:1 v/v). Humic acid was etherified using dimethylsulfate (DMS) in methanol-water solvent. It was studied about the kinetic of etherified humic acid adsorbing Au(III) and the effects of Sn(II) and Zn(II) in the system. Au(III) concentration was observed everytime by using AAS. Etherified humic acid both before and after interaction were characterized by using FTIR spectrometer, XRD, and microscopic photos. The results obtained show that the presence of Sn(II) and Zn(II) ions in the system of Au(III) adsorption on etherified humic acid would lowering its adsorption rate. Au(III) adsorption rate constant (k) without other metals exist, with the presence of Sn(II), and with the presence of Zn(II) are 6.44 x 10^-4 mg.gram^-1.minutes^-1; 2.79 x 10^-4 mg.gram^-1.minutes^-1; and 2.13 x 10^-4 mg.gram^-1.minutes^-1, respectively.

Kata Kunci : asam humat tereterifikasi, Au(III), kinetika adsorpsi, etherified humic acid, adsorption kinetic