INVESTIGASI PENGARUH UKURAN PARTIKEL, KONSENTRASI, DAN SIFAT MAGNETIK ADSORBEN NANOPARTIKEL Fe3O4 TERHADAP ADSORPSI LOGAM Co dan Fe DALAM LARUTAN

Dewi sartika, Dr. Edi Suharyadi, M.Eng.

2014 | Tesis | S2 Ilmu Fisika

Telah dilakukan proses purifikasi pada larutan yang mengandung logam berat Co dan Fe dengan menggunakan adsorben nanopartikel magnetit (Fe3O4). Pengaruh variasi ukuran partikel, konsentrasi adsorben, sifat magnetik remanen (Mr) dan amplifikasi terhadap penurunan kadar logam Fe dan Co dikaji dalam penelitian ini. Hasilnya diketahui bahwa adsorben Fe3O4 berukuran 11,5 nm mampu menjerap ion logam secara maksimal, ditandai dengan persentase penurunan kadar logam Fe dan Co masing-masing 99,855% dan 100%. Hal ini karena semakin kecil ukuran partikel semakin besar luas permukaa kontaknya. Selain itu, konsentrasi adsorben 0,005 g/ml dan 0,006 g/ml memberikan penurunan maksimal kadar maksimal logam Co dan Fe masing-masing sebesar 99,843% dan 100%. Penurunan kadar logam Co dan Fe maksimum terjadi pada nilai Mr 6,17 emu/cc yaitu masing-masing sebesar 99,936% dan 100%. Hal ini karena sifat magnetik yang besar menyebabkan penurunan kadar logam terjerap juga besar. Kata kunci: adsorpsi, adsorben, dan magnetit

Purification process on heave metal Co and Fe in liquid by using nanoparticle magnetit (Fe3O4) adsorbent have been investigated. The effect of particle size, concentration, remanence magnetic properties (Mr) and amplification to reduce of metal Fe and Co contents studied in this research. The result showed that the Fe3O4 adsorbent with the size of 11,5 nm was able to absorb the highest content of metal ions. Procentage of reduction of Fe and Co are 99.855% and100%, respectively. The particles which smaller particle have the higher contact surface. Moreover, concentration 0,005 g/ml and 0,006 g/ml gave the maximum reduction in the maximum degree of metals Co and Fe are 99.843% and 100%, respectively. The procentage of reduction of Co and Fe at Mr of 6,17 emu/cc are 99,936% dan 100%, respectively. The magnetic properties of absorbent would influence the reduction of metal contents. Key words: adsorption, adsorbent, and magnetite

Kata Kunci : adsorpsi, adsorben, dan magnetit