PREPARASI KARBON AKTIF DARI BERBAGAI JENIS BAMBU DAN KEMAMPUANNYA DALAM ADSORPSI UAP AIR DI DALAM UDARA

MUSTIKA DEWI MASITHOH, Dra. Ani Setyopratiwi, M,Si

2014 | Skripsi | KIMIA

Telah dilakukan preparasi karbon aktif dari berbagai jenis bambu secara aktivasi kimia dengan bahan pengaktif KOH dan aktivasi fisik pada pemanasan 600 °C dengan laju alir N2 30 mL/menit selama 1 jam pada temperatur tersebut. Tujuan penelitian ini untuk mengetahui karakteristik karbon aktif bambu pada adsorpsi uap air di kelembaban udara. Karakterisasi karbon aktif dilakukan dengan analisis luas permukaan dan volume pori (Surface Area Analyzer), Scanning Electron Microscopy (SEM), dan Fourier Transform Infrared (FT-IR) dan mutu karbon aktif di analisis sesuai dengan SII 0258-88. Analisis kemampuan adsorpsi uap air karbon aktif dilakukan pada kelembaban relatif 50-90%. Hasil menunjukkan karbon aktif bambu memiliki kadar abu 4,76-11,30%, kadar air 1,64-6,87%, bilangan iodin 237,30-357,22 mg/g. Karbon aktif bambu petung memiliki luas permukaan 260 m2/g, total volume pori 0,1618 cc/g dan jarijari pori 15,193 Å. Kemampuan adsorpsi uap air berhubungan dengan sifat pori dan gugus fungsi pada permukaan karbon aktif. Karbon aktif bambu petung memiliki adsorpsi uap air paling besar sekitar 0,148 g/g pada kelembaban relatif 90% .

Have performed preparation activated carbon from various kinds of bamboo using chemical and physical activation with KOH and by heating under 600 °C and N2 flow of 30 mL/min for 1 hour. The objective of this study is to characterize activated carbon obtained from bamboo as a precursor on water vapour adsorption under humid condition. Activated carbon was then analysed with surface area analyser, scanning electron microscopy, and fourier transform infrared (FT-IR) apparatus. The quality of the produced activated carbon was found to be acceptable under SII 0258-88 standard. Water vapour adsorption was then carried out under relative humidity of 50-90 %. The results show that activated carbon has an ash content of 4.76-11.30%, water content of 1.64-6.87%, iodine number of 237.30-357.22 mg/g. Petung activated carbon has a surface area of 260 m2/g, pore volume of 0.1618 cc/g and pore radius of 15.193 Å. Water vapor adsorption is related to the pore properties and availability of functional groups on the surface of activated carbon. Petung activated carbon shown the best water vapor adsorption around 0.148 g/g under relative humidity of 90%

Kata Kunci : bambu, karbon aktif, uap air, bilangan iodin