KAJIAN DINAMIKA SWELLING DARI SAMPEL-SAMPEL PLANAR MAIN-CHAIN LIQUID CRYSTAL ELASTOMER (MC-LCE) YANG DILARUTKAN DALAM KRISTAL CAIR NEMATIK

PARMAN, Dr. Yusril Yusuf, M.Eng.

2014 | Skripsi | FISIKA

Telah dilakukan penelitian secara eksperimen dinamika swelling pada sampel-sampel planar main-chain liquid crystal elastomer (MC-LCE), dengan variasi konsentrasi cross-linker (X) 8%, 12%, 14% dan 16% sebagai fungsi waktu. MC-LCE dilarutkan dalam wadah berisi larutan 5CB. Material MC-LCE akan bereaksi secara difusi ke dalam larutan 5CB akibat adanya perbedaan potensial kimia. Difusi larutan 5CB ke material MC-LCE menyebabkan MC-LCE mengembang (swollen) hingga mencapai kondisi setimbang. Pengamatan dinamika swelling pada sampel-sampel planar MC-LCE menunjukkan perubahan dimensi yang signifikan di sumbu-x maupun sumbu-y. Hasil eksperimen menunjukkan nilai parameter ekspansi panjang (𝛼𝑥𝑠𝑎𝑡) cenderung selalu menurun dan (𝛼𝑦𝑠𝑎𝑡) yang cenderung meningkat terhadap bertambahnya nilai konsentrasi cross-linker. Pada pengukuran dinamika swelling volume, nilai time constant cenderung meningkat seiring dengan bertambahnya konsentrasi cross-linker. Kata Kunci : Main-Chain Liquid Crystal Elastomer (MC-LCE), potensial kimia, difusi, parameter ekspansi panjang, time constant.

Experimentally research of swelling dynamics of planar main chain liquid crystal elastomer (MC-LCE) samples has been observed, with the variation of cross-linker consentration (X) 8%, 12%, 14%, and 16% as function of time. The planar samples MC-LCE is dissolved in a cell of 5CB. The material MC-LCE will react diffusion due to the difference of chemical potential. The diffusion of 5CB causes the material expands (swollen) until it reach an equilibrium condition. The observation of swelling dynamics of planar MC-LCE samples showed the significant dimensional changes of x-axis and y-axis. The result of experiment showed the value of length expansion parameter (𝛼𝑥𝑠𝑎𝑡) tend to decrease and (𝛼𝑦𝑠𝑎𝑡) tend to increase by the increasing of cross-linker consentration. On swelling dynamic volume, the value of time constant tend to increace by the increasing of cross-linker consentration. Keywords : main-chain liquid crystal elastomer (MC-LCE), chemical potential, diffusion, length expansion parameter, time constant.

Kata Kunci : Main-Chain Liquid Crystal Elastomer (MC-LCE), potensial kimia, difusi, parameter ekspansi panjang, time constant.