SERBUK PENGARUH SUHU KEMPA DAN KONSENTRASI PEREKAT CANGKANG KEPITING TERHADAP SIFAT FISIKA DAN MEKANIKA PAPAN PARTIKEL DARI TONGKOL JAGUNG

ALIFIA ZULFARAH K, Agus Ngadianto, S.Hut., M.Sc.

2014 | Tugas Akhir | D3 KEHUTANAN

Kebutuhan manusia akan kayu semakin meningkat, namun jumlah pasokan kayu justru berkurang. Selain itu, tingginya produk pertanian berbanding lurus dengan melimpahnya limbah yang dihasilkan dan merupakan salah satu permasalahan dalam kegiatan produksi pertanian yang perlu mendapat perhatian . Pengolahan dan pemanfaatan limbah pertanian diharapkan mampu mengatasi permasalah tersebut seperti pembuatan produk papan tiruan, yaitu papan partikel. Umumnya papan partikel banyak menggunakan perekat sintetis yang justru kurang ramah lingkungan dan tidak terbaharukan, sehingga perlu mencari alternatif lain untuk mengatasinya, yaitu dengan perekat berbasis kitosan yang berasal dari limbah cangkang kepiting. Bahan utama penelitian ini adalah limbah tongkol jagung dan perekat alami serbuk cangkang kepiting. Faktor yang digunakan adalah konsentrasi perekat konsentrasi 10%, 20%, dan 30% serta suhu pengempaan 160oC dan 180oC. Pembuatan papan partikel ini mengacu pada proses standar pembuatan papan partikel. Pengujian produk meliputi sifat fisika (kadar air, kerapatan, pengembangan tebal, dan penyerapan air) dan sifat mekanika (keteguhan rekat internal, modulus patah, dan modulus elastisitas) berdasarkan standar Japanese Industrial Standard untuk papan partikel (JIS A 5908 Tipe-8). Sifat papan partikel limbah tongkol jagung terbaik diperoleh dari perlakuan konsentrasi perekat 10% dan suhu pengempaan 180oC, dimana hanya nilai kadar air, kerapatan, dan keteguhan rekat internal yang memenuhi standar JIS A 5908 Tipe-8, dengan nilai kadar air 10,97%, kerapatan 0,876 g/cm2, pengembangan tebal 91,249%, penyerapan air 161,022%, keteguhan rekat internal 2,827 kg/cm2, modulus patah 39,328 kgf/cm2, dan modulus elastisitas 9.203,470 kgf/cm2,

The human need for wood is increasing, but the amount of wood supply is decreasing. In addition, the number of the agricultural products is directly proportional to the abundance of waste. It is one of the problems in the agricultural production activities that required attention. The processing and the utilization of the agricultural waste are expected to be able to solve these issues, such as the creation of artificial board products, i.e. particleboards. Generally particleboards use synthetic adhesives that are less environmentally friendly and renewable, making it necessary to find other alternatives to solve this problem, namely the chitosan-based adhesives that are derived from crab shell waste. The main material of this research is corncob waste and natural adhesive from crab shell. The factor used is the adhesive concentration of 10%, 20%, and 30% and the compression temperature of 160oC and 180oC. This particleboard manufacturing refers to the process of particleboard manufacturing standards. The testing products include physical properties (moisture content, density, thickness swelling, and water absorption) and mechanical properties ( internal bonding, modulus of rupture, and modulus of elasticity) based on the Japanese Industrial Standard for particle boards (JIS A 5908 Type-8). The best properties of particle boards from corncob waste were obtained from the treatment of 10% adhesive concentration and the temperature of 180oC, where only the value of the moisture content, density, and internal bonding meet the standards of JIS A 5908 Type-8, with a value of water content of 10,97%, density of 0,876 g/cm2, the thickness swelling of 91,249%, water absorption of 161,022%, internal bonding of 2,827 kg/cm2, modulus of rupture of 39,328 kgf/cm2, and modulus of elasticity of 9203,470 kgf/cm2.

Kata Kunci : Papan partikel, Tongkol jagung, Limbah cangkang kepiting, Sifat fisika, Sifat mekanika