ADSORPSI Ni(II) DALAM AIR MENGGUNAKAN KOMPOSIT ZEOLIT-MAGNETIT

ANIS KHOLIFATUR ROSYIDAH, Dr. Suyanta, M.Si.

2014 | Skripsi | KIMIA

Pada penelitian ini telah disintesis komposit zeolit-magnetit dan dipelajari aplikasinya untuk adsorpsi Ni(II). Sintesis komposit dilakukan menggunakan metode kopresipitasi campuran Fe2+ dan Fe3+ pada pH 11 dengan mempelajari pengaruh durasi pengadukan reaktan terhadap kristalinitas produk. Komposit zeolit-magnetit hasil sintesis dikarakterisasi dengan metode spektrofotometri Inframerah (FTIR) dan difraksi sinar-X (XRD). Aplikasi zeolit-magnetit sebagai adsorben Ni(II) dipelajari dengan mengkaji pengaruh pH dan kinetika adsorpsi. Uji pemisahan dilakukan untuk mendapatkan adsorben zeolit magnetit setelah proses adsorpsi. Hasil penelitian menunjukkan bahwa zeolit magnetit dengan kristalinitas paling baik terbentuk pada saat durasi pengadukan reaktan selama 1 menit. Komposit zeolit-magnetit hasil sintesis ini dapat menyerap Ni(II) secara optimal pada pH 6 dan mengikuti kinetika orde dua semu Ho dengan nilai konstanta laju adsorpsi (k) 1,45 x 10-3 g/mg menit. Pada kondisi yang sama zeolit teraktivasi dapat menyerap Ni(II) dengan nilai k sebesar 1,62 x 10-3 g/mg menit. Hasil uji recovery menunjukkan bahwa adsorben komposit zeolit-magnetit dapat dipisahkan dalam larutan menggunakan medan magnet eksternal lebih cepat dibandingkan zeolit teraktivasi. Kata kunci : komposit zeolit-magnetit, kopresipitasi, adsorpsi, uji recovery adsorben

Composite of zeolite-magnetite has been synthesized from FeSO4.5H2O and FeCl3 by coprecipitation method and applicated as magnetic adsorbent of Ni(II). The aim of this research is to improve the performance zeolite by modification using magnetite. Two gram of activated natural zeolite was added into 100 mL of Fe2+ and Fe3+ solutions with molar ratio of Fe2+ : Fe3+ ( 1:2 ). Then, the addition of 0.1 M NH4OH was forming the composite magnetic- zeolite with pH as high as 11 at 85 °C. The composite was sifted and washed by 10-4 M HCl until pH of 7. The effect of contact time was investigated using continue process. This magnetite adsorbent was characterized with X-ray diffraction and fourier transform infrared spectroscopy. The best contact time for synthesizing composite of zeolite magnetite was obtained at 1 minute. The optimum pH of the composite of zeolite magnetite adsorption capacities was 6. The kinetics data correlated well with the pseudo second order Ho equation with the value of rate constant (k) was 1.45 x 10-3 g/mg.min for composite of zeolit magnetite and 1.62 x 10-3 g/mg.min for the activated zeolite. The adsorbent of zeolite-magnetite composi te could be dispersed and removed quickly by external field magnet. Keywords: composite of zeolite-magnetite, coprecipitation, adsorption, kinetics model

Kata Kunci : komposit zeolit-magnetit, kopresipitasi, adsorpsi, uji recovery adsorben