KOMPOSIT KITOSAN/ZEOLIT SEBAGAI MATERIAL LEPAS-LAMBAT ION Cu(II)

ALEXANDRE BUDIMAN TASLIM, Dr. Yateman Arryanto

2014 | Skripsi | KIMIA

Preparasi komposit kitosan/zeolit sebagai material lepas-lambat Cu(II) telah dilakukan yang secara potencial dapat dimanfaatkan dalam bidang pertanian sebagai formulasi pupuk lepas-lambat. Telah dipelajari juga sifat pelepasannya dalam larutan asam sitrat 0,05 M. Komposit disintesis dengan mencampurkan hidrogel kitosan dengan zeolit alam 200 mesh serta larutan Cu(II) dan dilanjutkan dengan meneteskan campuran ke dalam larutan NaOH, kemudian dicuci dan dikeringkan. Variasi rasio kitosan dan zeolit dilakukan untuk mempelajari pengaruh rasio dalam sifat pelepasan komposit. Komposit yang diperoleh kemudian dikarakterisasi dengan menggunakan alat difraksi sinar-X, spektrofotometer inframerah, dan SEM serta sifat pelepasannya. Hasil karakterisasi SEM menunjukkan bahwa morfologi komposit menyerupai morfologi material penyusunnya. Adanya agregrasi zeolit pada permukaan menyebabkan morfologi kasar pada permukaan komposit. Pengujian pelepasan pada larutan asam sitrat 0,05 M menunjukkan bahwa dengan meningkatkan rasio kitosan terhadap zeolit, Cu(II) akan terlepas semakin cepat, dan sebaliknya, dengan meningkatkan rasio zeolit terhadap kitosan menyebabkan Cu(II) terlepas semakin lambat.

Chitosan/zeolite composite has been prepared as a polymer blend capable to slowly release Cu(II) species that could be potentially applied in the agricultural sector as a slow-release fertilizer formulation. Preparation of the composites is as follows, chitosan hydrogels were first mixed with zeolite 200 mesh and Cu(II) solution. The mixed solution was then added into NaOH solution drop-wisely, washed, filtered, and dried. The effects of various zeolite to chitosan ratio was studied against the Cu(II) release behaviour of the composites and was analysed in 0.05 M citric acid solution. The composites were characterized with X-ray diffraction apparatus, FT-IR spectrophotometer, and SEM and its release behaviour. The SEM images show that the morphology of the composites will follow the morphology of the major constituent available in the composite. Composite with a high zeolite ratio were shown to have a rough surface closely similiar with the morphology of zeolite surface due to the aggregation of zeolite in the surface of the composite. By increasing the ratio of chitosan to zeolite, the release rate of Cu(II) from the solution was found to be increased and vise versa.

Kata Kunci : komposit, kitosan, zeolit, Cu(II), sistem lepas-lambat