PENGARUH BAHAN BLEACHING IN-OFFICE TERHADAP PERUBAHAN KEKASARAN PERMUKAAN RESIN KOMPOSIT BULK FILL VISKOSITAS TINGGI DAN NANOFIL

WANDA SEPTYA EKATRA, drg. Tri Endra Untara, M.Kes., Sp.KG

2014 | Skripsi | PENDIDIKAN DOKTER GIGI

In-office bleaching merupakan salah satu perawatan gigi untuk mengembalikan warna gigi yang mengalami diskolorasi yang dilakukan oleh dokter gigi di tempat praktek. Seringkali pada pasien yang akan dilakukan bleaching terdapat restorasi resin komposit pada gigi anterior maupun posterior. Resin komposit terdiri dari berbagai macam, antara lain resin komposit bulk fill viskositas tinggi dan nanofil. Penelitian ini dilakukan untuk mengetahui perubahan kekasaran permukaan setelah prosedur in office bleaching pada restorasi resin komposit bulk fill viskositas tinggi dan nanofil. Subjek penelitian berupa 32 sampel resin komposit yang dibagi menjadi dua kelompok yaitu 16 sampel resin komposit bulk fill viskositas tinggi dan 16 sampel resin komposit nanofil berbentuk silinder dengan diameter 5 mm dan tinggi 2 mm. Subjek kemudian direndam dalam saliva buatan dan dimasukkan ke dalam inkubator selama 24 jam dengan suhu 37 0 C. Kekasaran awal resin komposit diukur dengan menggunakan alat surface roughness measuring instrument (Surfcom 120A). Selanjutnya subjek penelitian diaplikasikan bahan bleaching hidrogen peroksida 40% (Opalescense Boost, USA). Setelah itu, keseluruhan subjek diukur nilai perubahan kekasaran dan kemudian dilakukan analisis data menggunakan uji t tidak berpasangan dengan tingkat kepercayaan 95% (α=0,05). Rerata perubahan kekasaran permukaan pada kelompok I dan II berturut turut adalah 0,0662 ± 0,02705 µm dan 0,0475 ± 0,02295 µm. Analisis dengan uji t didapatkan perbedaan perubahan kekasaran permukaan resin komposit bulk fill viskositas tinggi dan nanofil (p<0,05). Kesimpulan yang diperoleh dari penelitian ini adalah perubahan kekasaran permukaan yang terjadi pada resin komposit bulk fill viskositas tinggi lebih besar dibandingkan resin komposit nanofil

In-office bleaching is one of a dental treatment that used to get back the colour of the discoloured teeth which applied by the dentist in the dentist’s office. Patient who need bleaching treatment, sometimes has already had composite resin restoration on their teeth. Composite resin have different types, such as bulk fill with high viscosity and nanofil composite resins. This research was conducted to determine changes in surface roughness after the procedure of in office bleaching on bulk fill with high viscosity and nanofil composite resin restorations. Thirty two cylinder-shaped specimens (5x2 mm) were prepared from each of the following materials: sixteen bulk fill with high viscosity composite resins and sixteen nanofil composite resins. Subjects was soaked in artificial saliva and put into incubator for 24 hours at 37 0 C. The initial surface roughness of composite resins were measured with a surface roughness measuring instrument (Surfcom 120A). After initial surface roughness measurement, subjects were applied with bleaching agent 40% hydrogen peroxide (Opalescense Boost, USA). Then, the final surface roughness were measured and the surface roughness change value was calculated. Data were analyzed using independent t-test at a 95% confidence level (α=0,05). The mean level in group I and II respectively 0,0662 ± 0,02705 µm and 0,0475 ± 0,02295 µm. T-test showed that there were difference in surface roughness change between bulk fill with high viscosity and nanofil composite resins (p<0,05). Based on the results, it can be concluded that the differences in surface roughness occurred between bulk fill with high viscosity and nanofil composite resins. Bulk fill with high viscosity composite resin had a greater surface roughness change than nanofil composite resins

Kata Kunci : Resin komposit bulk fill viskositas tinggi, resin komposit nanofil, in office bleaching, kekasaran permukaan