PERBEDAAN KEBOCORAN MIKRO SEMEN IONOMER KACA MODIFIKASI RESIN KONVENSIONAL DAN SEMEN IONOMER KACA MODIFIKASI RESIN NANO SEBAGAI BAHAN RESTORASI PADA GIGI DESIDUI (EKSPERIMENTAL LABORATORIS)

NATALIA, DR. drg. Indah Titien Soeprihati, SU., Sp.KGA(K)

2014 | Tesis | S2 Ilmu Kesehatan Gigi Anak

Salah satu bentuk kegagalan pelekatan bahan restorasi adalah terbentuknya celah di antara bahan restorasi dan struktur gigi, yang dikenal sebagai kebocoran mikro. Kebocoran mikro dipengaruhi oleh ukuran partikel bahan restorasi. Tujuan penelitian ini adalah untuk mengetahui perbedaan kebocoran mikro semen ionomer kaca modifikasi resin konvensional dan semen ionomer kaca modifikasi resin nano sebagai bahan restorasi pada gigi desidui. Penelitian eksperimental laboratoris dengan menggunakan 20 gigi insisivus desidui pasca ekstraksi dengan permukaan labial gigi dipreparasi menggunakan bur bulat yang berdiameter 2,5mm, lalu dibagi menjadi 2 kelompok masing-masing terdiri dari 10 gigi. Kelompok I ditumpat dengan semen ionomer kaca modifikasi resin konvensional dan kelompok II ditumpat dengan semen ionomer kaca modifikasi resin nano. Seluruh objek penelitian dilakukan thermocycling, seluruh bagian gigi dilapisi dengan cat kuku dan bagian apikal gigi ditutup dengan malam perekat, lalu direndam dalam larutan biru metilen dan selanjutnya gigi dibelah dengan arah labiopalatal. Pengamatan kebocoran mikro diamati dengan stereomikroskop dengan perbesaran 60x. Data dianalisis dengan uji T-tidak berpasangan menunjukkan bahwa terdapat perbedaan kebocoran mikro yang bermakna antara semen ionomer kaca modifikasi resin konvensional dan semen ionomer kaca modifikasi resin nano (p<0,05). Pada penelitian ini, dapat disimpulkan bahwa kebocoran mikro semen ionomer kaca modifikasi resin nano lebih besar dibandingkan semen ionomer kaca modifikasi resin konvensional ketika digunakan sebagai bahan restorasi pada gigi desidui. Kata kunci: kebocoran mikro, semen ionomer kaca modifikasi resin konvensional, semen ionomer kaca modifikasi resin nano

A kind of restoration adhesive failure is a gap between the restoration and the tooth structure, known as microleakage. Microleakage is influenced by particle size of restoration. Aim of this study is to compare the microleakage of conventional resin modified glass ionomer cement and nano resin modified glass ionomer cement in restorating deciduous teeth. Laboratory experiment was performed in 20 post extracted incisive deciduous teeth. The cavity was made by round bur, diameter 2,5mm. All of the teeth got separated into 2 groups. Group 1, 10 teeth were restorated with conventional resin modified glass ionomer cement and group 2, 10 teeth were restorated with nano resin modified glass ionomer cement. All teeth were then subjected to thermocycling. Each of tooth was covered with nail polish and the apices of all of the teeth were sealed with sticky wax. All of the teeth were immersed in blue dye and then they were sectioned labiopalatally. The specimen were then studied under stereomicroscope with a magnification 60x. Measurement of the depth of the blue dye infiltration was analyzed by independent sample T-test. It was known that there were significant correlation between microleakage of the teeth that were restorated with conventional resin modified glass ionomer cement and the teeth that were restorated with nano resin modified glass ionomer cement. Conclusion, conventional resin modified glass ionomer cement showed lower microleakage than nano resin modified glass ionomer cement in restorating deciduous teeth. Key words: microleakage, conventional resin modified glass ionomer cement, nano resin modified glass ionomer cement

Kata Kunci : kebocoran mikro, semen ionomer kaca modifikasi resin konvensional, semen ionomer kaca modifikasi resin nano