PEMBUATAN FILM KOMPOSIT KOMPLEKS POLIELEKTROLIT KITOSAN/κ -KARAGINAN DAN PEMANFAATANNYA SEBAGAI ADSORBEN METILEN BIRU

LIANA RIZKI OKTARI, Drs. Dwi Siswanta, M. Eng., Ph.D.

2014 | Tesis | S2 Ilmu Kimia

Film komposit kompleks polielektrolit (PEC) kitosan/κ­karaginan telah dibuat dan digunakan sebagai adsorben metilen biru (MB). Pembuatan film PEC dilakukan dengan mencampurkan kitosan dan κ­karaginan dalam media berair. Film yang terbentuk dikarakterisasi menggunakan spektroskopi Fourier Transform Infrared (FTIR) dan Scanning Electron Microscopy (SEM). Uji kemampuan adsorpsi dilakukan pada berbagai variasi perbandingan komposisi kitosan dan κ­karaginan, pH, waktu kontak, variasi konsentrasi metilen biru serta dilakukan juga kajian desorpsi pada pH asam dan penggunaan kembali film hasil desorpsi untuk mengadsorpsi MB sebanyak dua kali, semua perlakuan tersebut dianalisis menggunakan spektrofotometer UV­Vis. Hasil karakterisasi FTIR menunjukkan film berhasil disintesis dan karakterisasi menggunakan SEM menunjukkan adanya perubahan pada permukaan film sebelum dan sesudah adsorpsi serta setelah desorpsi. Pada proses adsorpsi, film dengan perbandingan komposisi 40:60 antara kitosan dan κ­ karaginan menunjukkan kemampuan adsorpsi MB tertinggi pada larutan dengan pH netral. Adsorpsi mengalami kesetimbangan di menit ke 15 dan kinetikanya mengikuti orde dua semu. Proses adsorpsi MB sesuai dengan persamaan isoterm Langmuir dengan kapasitas adsorpsi maksimum mencapai 425,35 mg/g. Film dapat dipergunakan kembali untuk mengadsorpsi MB setelah dilakukan proses desorpsi pada medium dengan pH 2. Hasil­hasil tersebut menunjukkan bahwa penggunaan komposit film PEC kitosan/κ­karaginan pada penelitian ini berpotensi sebagai adsorben untuk mengadsorpsi MB

The chitosan/κ­carrageenan polyelectrolyte complex (PEC) composite films had been synthesized and tested as adsorbents for the removal of methylene blue (MB). The films were prepared by mixing chitosan and κ­karaginan in aqueous solution. Films were then characterized using Fourier Transform Infrared (FTIR) spectroscopy and Scanning Electron Microscopy (SEM). Adsorption capabilities were studied by varying the chitosan and κ­carrageenan composition ratios, pH, time contacts and concentrations of MB while the desorptions were conducted at acidic solutions. The reusabilityof adsorbent for MB adsorption after desorption was also studied and the films were used to adsorp MB twice. All these treatments were analyzed using UV­Vis spectrophotometer. The synthesis film was succeed as shown in FTIR results and the surface morphology of film was changed before and after adsorption also after desorption as shown in SEM results. The MB uptake of the film with 40:60 ratios of chitosan and κ­carrageenan was the highest in neutral pH conditions. Pseudo­second­order equation predicted well the kinetics of adsorption with the adsorption achieved within 15 min. The film showed the maximum adsorption capacity of MB at 425.35 mg/g and the adsorption followed Langmuir isotherm model. This adsorbent was also able to be reused for the adsorption of MB, after desorption process using distilled water at pH 2. Therefore, the use of chitosan/κ­carrageenan PEC composite film in this work proved to be promising adsorbent for removing methylene blue from aqueous solutions

Kata Kunci : metilen biru; adsorpsi; film komposit PEC kitosan/κ-karaginan