ZEOLIT TERMODIFIKASI MAGNETIT BERBASIS METODE KOPRESIPITASI SEBAGAI ADSORBEN Zn(II)

NURINA ADLIN, Dr. Suyanta, M.Si.

2014 | Skripsi | KIMIA

Telah dilakukan zeolit termodifikasi magnetit berbasis metode kopresipitasi sebagai adsorben Zn(II). Sebanyak 2 g zeolit teraktivasi dimasukkan ke dalam larutan yang mengandung Fe3+ dan Fe2+ dengan konsentrasi masingmasing 0,1 M dan 0,05 M. Selanjutnya campuran diaduk selama 1 menit pada temperatur 85 °C, kemudian ditambahkan NH4OH 1,3 M tetes demi tetes hingga pH 11. Endapan disaring, dicuci HCl 10-4 M hingga pH netral, dan dikeringkan pada temperatur 100 °C selama ± 2,5 jam, lalu dikarakterisasi dengan XRD dan FTIR. Prosedur serupa dilakukan untuk mengetahui pengaruh rasio molar Fe3+/Fe2+ 1:2 dan 1:1 serta variasi konsentrasi pada rasio molar tetap Fe3+/Fe2+ 2:1. Hasil penelitian menunjukkan bahwa kondisi optimal modifikasi magnetik pada zeolit adalah pada rasio molar Fe3+/Fe2+ 2:1 dengan konsentrasi masingmasing 0,025 M dan 0,00125 M. Adsorpsi optimal Zn(II) diperoleh pada pH 5 dan mengikuti kinetika pseudo orde dua dengan konstanta laju adsorpsi 1,917×10-3 g/mg.menit untk zeolit teraktivasi dan 3,989×10-3 g/mg.menit untuk zeolit termodifikasi magnetit. Uji recovery setelah aplikasi menunjukkan zeolit termodifikasi magnetit memerlukan waktu lebih singkat dibandingkan zeolit teraktivasi dengan bantuan medan magnet eksternal. Kata kunci: zeolit, zeolit termodifikasi magnetit, pseudo orde dua, konstanta laju adsorpsi

Magnetically modified zeolite has been prepared using coprecipitation method and used as an adsorbent of Zn(II). Two grams of activated zeolite was added into Fe3+ and Fe2+ solution with concentration of 0.1 M and 0.05 M, respectively. Furthermore the mixture was stirred for 1 minute at 85 °C, then 1.3 M NH4OH was added dropwise until pH 11. The precipitate was filtered, washed by HCl 10-4 M until pH neutral, and dried at 100 °C for ± 2,5 hours, then characterized by XRD and FTIR. The same procedure was also carried out for understanding the influenced of Fe3+/Fe2+ molar ratio and performed under 1:2 and 1:1 variations; also for the influence of variations in Fe3+/Fe2+ concentrations with a fixed molar ratio 2:1. The results showed that the optimum condition magnetite modified zeolite was Fe3+: Fe2+ molar ratio 2:1 with 0.025 M and 0.00125 M, respectively. The optimum adsorption of Zn(II) was obtained at pH 5 and the kinetic coincide well second pseudo order with adsorption rate constant of 1.917×10-3 g/mg.menit for the activated zeolite and 3.989×10-3 for magnetite modified zeolite. The recovery test after an application showed that magnetite modified zeolite require less time than activated zeolite with an external magnetic field. Keywords: zeolite, magnetite modified zeolite, pseudo second order, adsorption rate constant

Kata Kunci : zeolit, zeolit termodifikasi magnetit, pseudo orde dua, konstanta laju adsorpsi, zeolite, magnetite modified zeolite, pseudo second order, adsorption rate constant