PERBANDINGAN KEKUATAN GESER PELEKATAN SEMEN IONOMER KACA KONVENSIONAL DAN SEMEN IONOMER KACA MODIFIKASI RESIN PADA DENTIN DALAM PERENDAMAN SALIVA pH 7 DAN 5

DENTISIA A SHABAHATI, drg. Pribadi Santosa, M.S., Sp.KG.

2014 | Skripsi | PENDIDIKAN DOKTER GIGI

Derajat keasaman rongga mulut yang rendah dapat menurunkan sifat mekanis material restorasi gigi. Tujuan peneltian ini adalah untuk mengetahui perbedaan kekuatan geser pelekatan SIK konvensional dan SIKMR pada dentin dalam perendaman saliva pH 7 dan 5. Penelitian dilakukan pada 28 buah gigi premolar maksila yang masih utuh dan bebas karies hasil pencabutan. Permukaan bukal gigi dipotong dan dihaluskan, sehingga didapatkan dentin yang halus dan rata dengan diameter minimal 3mm. Semua sampel difiksasi dalam balok resin akrilik dengan panjang rusuk 10 mm. Sampel ditumpat SIK dengan diameter 3 mm dan tinggi 2 mm, lalu dibagi menjadi 4 kelompok secara acak, yaitu kelompok I sebagai kelompok SIK konvensional dalam perendaman saliva pH 7, kelompok II sebagai kelompok SIKMR dalam perendaman saliva pH 7, kelompok III sebagai kelompok SIK konvensional dalam perendaman saliva pH 5, kelompok IV sebagai kelompok SIKMR resin dalam perendaman saliva pH 5. Seluruh sampel direndam dalam saliva tiruan selama 7 hari. Kekuatan geser pelekatan diukur menggunakan Universal Testing Machine dengan kecepatan geser 0,5 mm/menit. Hasil rerata kekuatan geser pelekatan kelompok I,II,III,IV secara berurutan adalah 2,65±0,85 MPa; 8,84±2,49 MPa; 2,10±0,45 MPa; 2,10±0,45 MPa; 7,37±3,52 MPa. Hasil uji ANAVA dua jalur menunjukkan bahwa terdapat pengaruh jenis SIK terhadap kekuatan geser pelekatan (p<0,05), tidak terdapat pengaruh pH saliva terhadap kekuatan geser pelekatan SIK (p>0,05), serta tidak terdapat interaksi antara jenis SIK dan pH saliva terhadap kekuatan geser pelekatan pada dentin (p>0,05). Kesimpulan dari penelitian ini adalah tidak terdapat perbedaan kekuatan geser pelekatan SIK konvensional dan SIKMR pada dentin dalam perendaman saliva pH 7 dan 5. SIKMR mempunyai kekuatan geser pelekatan yang lebih tinggi dibandingkan SIK konvensional dalam pH saliva yang berbeda.

The mechanical properties of tooth restorative materials depend on oral acidity. The aim of this research was to examine the shear bond strength of conventional GIC and RMGIC on dentin as a result of immersion in saliva of pH 7 and 5 . This study was conducted on 28 samples of caries-free extracted maxillary premolars. Buccal surface of each tooth was cut to reach the opened and flattened dentin with diameter of at least 3mm. Buccal surface of each tooth was cut and flattened until the dentin with diameter of at least 3 mm was exposed. all samples were embedded in acrylic resin block and GIC filled the cavity with diameter of 3 mm and 2 mm in height. All samples were divided randomly into 4 groups, namely group I as conventional GIC group in saliva of pH 7 immersion, group II as RMGIC group in saliva of pH 7 immersion, group III as conventional GIC group in saliva of pH 5 immersion, the group IV as a group RMGIC in saliva of pH 5 immersion. All samples were immersed in artificial saliva for 7 days. The shear bond strength was measured by using Universal Testing Machine with a shear load speed of 0.5 mm / minute . The mean of shear bond strength of group I,II,III,IV were 2,65±0,85 MPa; 8,84±2,49 MPa; 2,10±0,45 MPa; 2,10±0,45 MPa; 7,37±3,52 MPa. The statistical analysis using two ways ANOVA revealed that there was a significant difference between type of GIC to shear bond strength on dentin (p<0,05). There was no significant difference between pH of saliva to shear bond strength of GIC on dentin, and no interaction between type of GIC and pH of saliva to shear bond strength on dentin (p>0,05). The conclusion could be drawn that there was no difference of shear bond strength of conventional GIC and RMGIC immersing in saliva of pH 7 and 5. RMGIC had the higher shear bond strength in different pH of saliva immersion.

Kata Kunci : SIK konvensional, SIKMR, kekuatan geser pelekatan, saliva pH 7, saliva pH 5