PENGARUH PENAMBAHAN POLIGLISEROL TERHADAP KARAKTER MINYAK JARAK KEPYAR (Ricinus communis L.) SEBAGAI BAHAN DASAR MINYAK PELUMAS

FENZY PUTRI LIEWENTI, Prof. Dr. Triyono, S.U

2014 | Skripsi | KIMIA

Telah dilakukan penelitian untuk mengetahui pengaruh penambahan poligliserol terhadap karakter minyak jarak kepyar (Ricinus communis L.) sebagai bahan dasar minyak pelumas. Dilakukan penambahan poligliserol terhadap minyak jarak kepyar dengan variasi perbandingan 2:20, 3:20, 4:20, 5:10, dan 6:20 (b/v). Poligliserol merupakan zat aditif yang diperoleh dari hasil polimerisasi gliserol yang direaksikan dengan katalis KOH pada suhu 190 oC sambil diaduk selama 6 jam. Zat aditif ini kemudian dicampurkan ke dalam minyak jarak kepyar (Ricinus communis L.) sehingga diperoleh minyak pelumas hasil “Top Green RG”. Karakter fisik minyak pelumas ditentukan dengan metode ASTM, antara lain uji kerapatan spesifik 60/60 oF, viskositas kinematik pada temperatur 40 oC dan 100 oC, titik nyala, dan titik kabut. Sedangkan perubahan karakter kimia dianalisis dengan Spektroskopi Inframerah (IR) dan Kromatografi Gas (GC). Hasil penelitian menunjukkan bahwa penambahan poligliserol meningkatkan viskositas minyak pelumas. Hasil uji viskositas ini sesuai dengan minyak pelumas standar pada perbandingan 6:20. Hasil viskositas ini sesuai dengan viskositas MASRI RG pelumas roda gigi industri. Minyak pelumas hasil ini memiliki keunggulan pada kerapatan spesifik, indeks viskositas, nilai pemanasan kotor (GHV), dan nilai pemanasan bersih (NHV), sedangkan kelemahannya adalah memiliki titik nyala dan titik kabut. Hasil analisis Spektroskopi Inframerah (IR) dan Kromatografi Gas (GC) menunjukkan adanya interaksi antara zat aditif (poligliserol) dan minyak jarak kepyar (Ricinus communis L.) sebagai bahan dasar dan tidak membentuk senyawa baru sebagai pelumas

Effects of polyglycerol addition into castor oil (Ricinus communis L.) character as the base material of lubricant has been studied. Polyglycerol was added into castor oil in mass to oil volume variations of 2:20, 3:20, 4:20, 5:20 and 6:20. Polyglycerol as an additive substance obtained from the polymerization of glycerol using KOH as a polymerization catalyst in 190 °C under constant stirring time for 6 hours. The additive substance was then added into the base oil to obtain the lubricant oil product “Top Green RG”. The physical properties of the lubricant were determined based on ASTM method, which were found to have a specific density of 60/60 oF, kinematic viscousity at 40 °C and 100 °C, flash point, and cloud point. The chemical character of the lubricant was then analysed using IR spectroscopy and GC. The result of this study showed that the addition of polyglycerol increase the viscousity of the base oil. The viscousity test showed in accordance with lubricant standard comparing additive and base material at 6:20. This result accordance with MASRI RG lubricant product coqwheel’s industry. This lubricant’s result have excellent specific gravity, index viscousity, gross heating value, and nett heating value, whereas the weakness are flash point and cloud point. The result of Infrared Spectroscopy and Gas Chromatography showed that there are interaction between additive (polyglycerol) and Ricinus communis L. as base material of lubricant and was not formed new molecule as lubricant

Kata Kunci : pelumas, minyak jarak kepyar (Ricinus communis L.), poligliserol.