EFEK MAGNETISASI ZEOLIT ALAM TERHADAP KRISTALINITAS, SIFAT PORI DAN KINERJANYA SEBAGAI ADSORBEN Pb(II)

IRENE FERANDY PATRIC, Dr. Suyanta, M.Si.

2014 | Skripsi | KIMIA

Telah dilakukan magnetisasi zeolit alam untuk memperoleh adsorben yang memiliki sifat kemagnetan dengan mengkaji pengaruh temperatur dan pH terhadap jenis oksida besi yang terbentuk serta pengaruhnya terhadap kristalinitas, sifat pori dan kinerjanya sebagai adsorben Pb(II). Sebanyak 2 g serbuk zeolit teraktivasi dimasukkan ke dalam 100 mL larutan yang mengandung Fe2+ dan Fe3+ (rasio molar 1:2) dan ditambahkan larutan NH4OH hingga pH 9 pada temperatur 28 °C. Endapan disaring dan dicuci dengan larutan HCl 10-4M hingga netral. Padatan yang diperoleh dioven pada temperatur 100 oC selama 1 jam. Prosedur serupa dilakukan kembali untuk mengetahui pengaruh temperatur dan pH. Karakterisasi dilakukan dengan metode FTIR, XRD dan fisisorpsi N2. Hasil penelitian menunjukkan bahwa kondisi optimal pembuatan komposit zeolit-magnetit adalah pada temperatur 85oC dan pH 11. Adsorpsi optimal Pb(II) oleh adsorben tercapai pada pH 5 dan mengikuti model kinetika pseudo orde dua dengan tetapan laju adsorpsi 0,021 (g/mg menit) untuk adsorben zeolit teraktivasi dan 0,075 (g/mg menit) pada komposit zeolit-magnetit. Magnetisasi zeolit memperlihatkan perubahan ukuran pori dari mikropori menjadi mesopori. Uji recovery setelah aplikasi fasa padat menggunakan komposit zeolit-magnetit memerlukan waktu lebih cepat dibanding menggunakan adsorben zeolit teraktivasi.

The effects of natural zeolite magnetization toward its crystallinity, porosity and performance as a magnetism adsorbent to recover Pb(II) has been conducted. The magnetic zeolite has also been studied its temperature and pH effects regarding with the iron species. Two gram of activated natural zeolite was added into 100 mL of Fe2+ and Fe3+ solutions with molar ratio of Fe2+ : Fe3+ ( 1:2 ). Then, the addition of 0.1 M NH4OH was forming the composite magneticzeolite with pH as high as 9 at 28 °C. The composite was sifted and washed by 10-4 M HCl until pH of 7. It was heated up to 100 oC for an hour. Same procedure was also carried out for understanding the influence of temperature and pH. Characterizations were performed by using infrared spectrometry, X-ray diffractometry and N2 physicosorption. The result showed that optimum condition of zeolite-magnetite sythesis is heating at 85 oC and pH of 11. The optimum pH of Pb(II) adsorption was 5 and the kinetic model fits with second pseudo orde of kinetic model with rate constant of 0.021 (g/mg.min) for the activated zeolite adsorbent and 0.075 (g/mg.min) on the composite zeolite-magnetite. The effect of magnetization showed the transformation of porosity of zeolite from microporous to mesoporous material. The recovery test after its performance zeolite-magnetite composite needs quicker time than activated zeolite.

Kata Kunci : zeolit, komposit zeolit-magnetit, pseudo orde dua, tetapan laju adsorpsi, mesopori.