SIFAT FISIKA MEKANIKA DAN KETAHANAN TERHADAP RAYAP KAYU KERING PADA PAPAN PARTIKEL BAMBU PETUNG DENGAN ASAM SITRAT

Ari Puspa Yudha, Dr. Ragil Widyorini, S.T., M.T.,

2013 | Tesis | S2 Ilmu Kehutanan

Meningkatnya kebutuhan terhadap papan partikel dari bahan baku berlignoselulosa perlu diimbangi dengan kualitas produk, utamanya bahan baku yang digunakan dengan teknologi dan bahan-bahan yang ramah lingkungan. Pada penelitian ini diketahui pengaruh asam sitrat terhadap sifat fisika mekanika dan ketahanan terhadap rayap kayu kering papan partikel. Partikel dipersiapkan dari Dendrocalamus asper Backer yang dicampur dengan larutan asam sitrat dari 0% hingga 40%. Campuran tersebut dikempa pada suhu 200°C dan 220°C menggunakan tekanan kempa 2 MPa selama 15 menit. Kestabilan dimensi (penyerapan air dan pengembangan tebal) dan ketahanan terhadap serangan rayap kayu kering meningkat seiring peningkatan asam sitrat. Sifat mekanika dipengaruhi oleh persentase asam sitrat yang diberikan dan papan partikel yang dibentuk dengan asam sitrat 30% menunjukkan sifat terbaik. Nilai rata-rata keteguhan rekat internal, modulus patah, dan modulus elastisitas pada penambahan asam sitrat 30%, masing-masing sebesar 0,32 MPa, 14,95 MPa, dan 4,26 GPa. Berdasarkan hasil Fourier Transform Infrared Spectroscopy, intensitas antara gugus hidroksil dari partikel dengan karboksil dari asam sitrat (puncak di sekitar 1720 cm-1) semakin meningkat seiring penambahan asam sitrat.

Development of natural adhesives that does not depend on fossil resources is very important for the future of particleboard materials. We recently found that citric acid can be used as a natural adhesive for particleboard. In this study, we investigated the properties of physical mechanical and dry-wood termite resistance on bamboo particleboard with citric acid. Particle obtained from Dendrocalamus asper Backer was mixed with citric acid ranging from 0% to 40%, and the particle mixture was pressed at a temperature 200°C and 220°C. The press pressure and heating time were set at 2 MPa and 15 minutes, respectively. Water resistance increased with citric acid, and termite resistance were also clearly increased with citric acid content. The mechanical properties were affected by the citric acid content, and the particleboard fabricated at 30% citric acid showed excellent values. The average modulus of rupture, modulus of elasticity, and internal bonding at 30% was 14.95 MPa, 4.26 GPa, and 0.32 MPa, respectively. Based on the results of Fourier Transform Infrared Spectroscopy, intensity of ester linkages between bamboo and citric acid were increased with citric acid content.

Kata Kunci : Papan partikel, asam sitrat, fisika-mekanika, ketahanan rayap kayu kering, bambu petung