STUDI TRANSPOR UREA PADA MEMBRAN POLIELEKTROLIT KITOSAN-PEKTIN

GOVIRA CHRISTIADORA ASBANU, Dr. Dwi Siswanta, M.Eng.

2013 | Tesis | S2 Ilmu Kimia

Penelitian mengenai studi transpor urea pada membran polielektrolit (PEC) kitosan-pektin telah dilakukan. Kajian transpor dilakukan pada membran PEC kitosan-pektin non MIP (Molecularly Imprinted Polymer) dan MIP dengan molekul pencetak urea. Kajian ini bertujuan untuk mengetahui pengaruh variasi komposisi kitosan dan pektin pada membran PEC terhadap hasil transpor urea, pengaruh membran PEC kitosan-pektin MIP terhadap hasil transpor dan pengaruh kompetisi urea, kreatinin dan vitamin B12 terhadap hasil transpor. Membran PEC kitosan-pektin non MIP maupun MIP disintesis dari paduan kitosan dan pektin. Pada membran PEC kitosan-pektin MIP ditambahkan urea sebagai molekul pencetak. Hasil sintesis dikarakterisasi dengan spektrofotometer inframerah. Kajian meliputi optimasi perbandingan komposisi kitosan dan pektin serta transpor urea pada membran PEC non MIP dan MIP dengan variasi konsentrasi yang diamati pada berbagai interval waktu. Hasil karakterisasi membran PEC kitosan-pektin menunjukkan bahwa telah terjadi pergeseran serapan gugus amino kitosan dan gugus karboksil pektin pada bilangan gelombang 1604 cm-1 disebabkan interaksi ionik antara gugus amino kitosan dan gugus karboksil pektin. Membran PEC kitosan-pektin dengan komposisi 70:30 merupakan yang terbaik. Hasil transpor dan fluks urea pada membran PEC kitosan-pektin MIP lebih besar dibandingkan membran non MIP. Hasil transpor dan fluks membran MIP urea 1000 ppm (42.32%; 3,92×10-3 g/m2s), 1500 ppm (37.23%; 4,56×10-3 g/m2s), dan 2000 ppm (34.99%; 5,07×10-3 g/m2s). Hasil transpor dengan fasa sumber yang terdiri atas 2 senyawa (urea dan kreatinin) dan 3 senyawa (urea, kreatinin dan vitamin B12) menunjukkan bahwa persen transpor urea pada membran MIP lebih besar dibandingkan pada membran non MIP.

Urea transport studies on chitosan-pectin polyelectrolyte (PEC) membrane have been done. Membrane transport studies conducted at non MIP (Molecularly Imprinted Polymer) PEC membrane and MIP membrane that imprinted by urea. The purpose of this study is to determine the effect of variations compotition of chitosan and pectin on PEC membrane to transport results of urea, the effect of membrane PEC MIP that imprinted by urea to transport results and the effect of competition urea, creatinine and vitamin B12 to the results of the transport. PEC chitosan-pectin non MIP and MIP membranes are synthesized from chitosan and pectin. At PEC chitosan-pectin MIP membranes is added urea as a template molecule. Synthesized results were characterized by spectrofotometer IR. Studies are include optimization of the composition ratio of chitosan and pectin and urea transport with various concentration that observed at various time intervals. PEC chitosan-pectin membrane characterization with IR spectrophotometer indicate that there has been an ionic interactions between the amino groups of chitosan and the carboxyl group of pectin in the wave number 1604 cm-1. The best result of transport membrane composition ratio was 70:30. The transport and flux results of chitosan-pectin PEC MIP membrane is higher than non MIP membrane. The results of transport and flux of chitosan-pectin PEC MIP membrane are 1000 ppm (42.32%; 3,92×10-3 g/m2s), 1500 ppm (37.23%; 4,56×10-3 g/m2s), and 2000 ppm (34.99%; 5,07×10-3 g/m2s). Transport results of source phase that include 2 component (urea and creatinine) and 3 component (urea, creatinine and vitamin B12) indicate that transport result of MIP membrane is higher than non MIP membrane.

Kata Kunci : polielektrolit, kitosan, pektin, urea, membran