KOMPOSIT KITOSAN-ZEOLIT SEBAGAI SISTEM LEPAS LAMBAT BESI(III)

RIVA ISMAWATI, Dr. Yateman Arryanto,

2013 | Tesis | S2 Ilmu Kimia

Telah dilakukan preparasi material lepas lambat ion Fe(III) dengan menggunakan kitosan dan zeolit serta evaluasi sifat pelepasannya dalam larutan asam sitrat 0,33 M. Komposit dibuat dengan mencampurkan zeolit, gel kitosan, dan larutan Fe(III), kemudian meneteskan campuran ke dalam larutan NaOH. Sintesis komposit dilakukan dengan memvariasi masa kitosan maupun zeolit. Karakterisasi struktur komposit dilakukan dengan menggunakan spektrofotometer inframerah dan difraksi sinar-X. Morfologi permukaan komposit dianalisis dengan menggunakan SEM, peranan rantai kitosan dalam menutup zeolit-Fe dianalisis dengan menggunakan TEM, sedangkan stabilitas termal komposit dianalisis dengan menggunakan TGA. Foto SEM menunjukkan secara jelas morfologi kasar, agregasi zeolit-Fe, dan rongga besar dengan bertambahnya masa zeolit dalam komposit sedangkan, morfologi komposit halus tanpa agregasi zeolit-Fe, dan rongga besar yang berarti dengan bertambahnya masa kitosan. Gambar dark field (DF) dari TEM mengkonfirmasi bahwa daerah terang zeolit-Fe menjadi semakin tidak teramati dalam komposit dengan masa kitosan tinggi. Pengujian sifat pelepasan komposit dalam larutan asam sitrat 0,33 M menunjukkan bahwa ion Fe(III) dilepaskan lambat dari komposit dengan masa zeolit tinggi dan memilki efisiensi pelepasan Fe(III) rendah. Namun, ion Fe(III) dilepaskan cepat dari komposit dengan masa kitosan tinggi dan memiliki efisiensi pelepasan Fe(III) tinggi.

Preparation of an iron(III) slow release materials using chitosan and zeolite and evaluation of their release behavior in the 0.33 M citric acid solution have been done. The composites were prepared by mixing zeolite, chitosan gel, and Fe(III) solution, then the mixture was dripped into NaOH solution. Composite synthesis was carried out by varying the mass of chitosan and zeolite. The structure of composites was characterized using infrared spectrophotometer and X-ray diffraction. Composite surface morphology was analyzed using SEM, the role of chitosan chain in covering zeolite-Fe was analyzed using TEM, while the thermal stabilities of composites were analyzed using TGA. The morphology that was The SEM images showed obviously the rough morphology, zeolite-Fe aggregation, and void formation with the increase of zeolite mass. smooth without appreciable zeolite-Fe aggregation and void could be observed from the SEM image of the composites with the increase of chitosan mass. The dark field (DF) image of TEM confirmed that the bright region of zeolite-Fe became more unobservable in the composite with high chitosan content. The testing of composite release behavior in the 0.33 M citric acid solution showed that Fe(III) ions were released slowly from the composites with high zeolite mass content and it had low release efficiency. However, Fe(III) ions were released quickly from the composites with high chitosan mass content and it had high release efficiency.

Kata Kunci : kitosan, zeolit, komposit, lepas lambat Fe(III)