PENGARUH PASTA GIGI DENGAN KANDUNGAN ALUMINIUM OXIDE TERHADAP KEKASARAN PERMUKAAN PLAT GIGI TIRUAN RESIN AKRILIK POLIMERISASI PANAS

NELA ANGGUN S, drg. Suparyono Saleh, Sp.Pros.(K).

2013 | Skripsi | PENDIDIKAN DOKTER GIGI

Pasta gigi merupakan salah satu bahan pembersih gigi tiruan secara mekanik melalui penyikatan. Pasta gigi mengandung berbagai macam bahan abrasif seperti aluminium oxide. Aluminium oxide memiliki kekerasan permukaan yang tinggi sehingga memungkinkan keausan permukaan yang lebih tinggi. Kekasaran permukaan gigi tiruan dapat memicu perlekatan mikroorganisme. Tujuan penelitian ini adalah untuk mengetahui pengaruh pasta gigi dengan kandungan aluminium oxide terhadap kekasaran permukaan plat gigi tiruan resin akrilik polimerisasi panas. Penelitian ini dilakukan dengan penyikatan pada 32 sampel plat resin akrilik polimerisasi panas berukuran 20 x 10 x 3 mm. Setelah dilakukan pengukuran kekasaran awal, sampel dibagi menjadi 2 perlakuan, yaitu disikat dengan pasta gigi yang mengandung aluminium oxide (n=16) dan disikat dengan pasta gigi tanpa kandungan aluminium oxide (n=16). Penyikatan dilakukan dengan mesin penyikat berkecepatan 356 gerakan bolak-balik per menit dan beban 200 g selama 250 menit. Kekasaran permukaan akhir sampel diukur dengan alat pengukur kekasaran permukaan (Surfcom 120A). Data dianalisis menggunakan t-test dengan signifikansi 95% (α=0,05). Hasil penelitian menunjukkan rerata peningkatan kekasaran permukaan yang lebih tinggi pada sampel yang disikat menggunakan pasta gigi dengan kandungan aluminium oxide. Berdasarkan analisis t-test diperoleh nilai p < 0,05 yang menunjukkan terdapat perbedaan peningkatan kekasaran permukaan yang bermakna antara kedua kelompok perlakuan.

The removal debris via the use of toothbrush and toothpaste is a mechanical method of denture cleansing. There are various types of abrasive materials used in contemporary toothpaste which is effective in the removal of stain, for example aluminium oxide. But, aluminium oxide can lead to greater abrasiveness due to its hardness. Surface roughness on denture is one of the main problems in the oral cavity because it can lead to adhesion of microorganisms. The purpose of this study was to analyze the effects of the toothpastes containing aluminium oxide on the surface roughness of heat-polymerized acrylic resins. This study used 32 samples heat-polymerized acrylic resins measuring 20 x 10 x 3 mm. After the initial roughness measurement, the sample was divided into 2 groups, which is brushed with toothpastes containing aluminium oxide (n = 16) and brushed with control toothpastes (n = 16). Brushing was conducted in a brushing machine with a rate of 356 brush strokes per minute for 250 minutes. The final roughness was measured using surface roughness measuring instrument. Results data were analyzed using t-test with a significance of 95% (α = 0.05). The results showed that group which is brushed with toothpaste containing aluminium oxide caused more surface roughness than group which is brushed with control toothpastes. Based on the analysis of the t-test, p-value < 0.05 showed that there are significant differences of the increasing value of surface roughness between the two groups.

Kata Kunci : kekasaran permukaan, resin akrilik, pasta gigi, aluminium oxide