PERBEDAAN WAKTU SETTING SEMEN ALPHA TRICALCIUM PHOSPHATE (α-TCP) PADA PENGGUNAAN CAIRAN DISODIUM HYDROGEN PHOSPHATE (Na2HPO4) DAN SODIUM DIHYDROGEN PHOSPHATE (NaH2PO4)

ARUM NUR KARTIKA PUTRI, Dr. drg. Indah Titien Soeprihati, SU., Sp. KGA.

2013 | Skripsi | PENDIDIKAN DOKTER GIGI

Semen kalsium fosfat diteliti sebagai biomaterial untuk substitusi dan regenerasi tulang. Alpha tricalcium phosphate adalah salah satu contoh dari semen kalsium fosfat. Semen α-TCP memiliki beberapa kelebihan, di antaranya mudah dimanipulasi, mengeras pada keadaan in vivo, dan biocompatible. Reaksi setting semen α-TCP dimulai sesaat setelah pencampuran pasta semen dan akan setting setelah beberapa menit. Waktu setting semen α-TCP dipengaruhi oleh beberapa faktor, misalnya jenis cairan sebagai campuran serbuk α-TCP. Pada penelitian ini, efek larutan fosfat pada waktu setting semen α-TCP diamati menggunakan dua jenis larutan fosfat: 0,2 mol/L Na2HPO4 and 0,2 mol/L NaH2PO4. Serbuk semen sebanyak 500 mg dicampur dengan cairan sebanyak 250 μl di atas glass plate. Setelah pengadukan selama 1 menit pada suhu ruang, pasta dimasukkan ke dalam cetakan Teflon dengan diameter 10 mm dan tinggi 2,5 mm. Waktu initial setting pada suhu 370C diukur dengan jarum Gillmore. Rerata dan standar deviasi dari waktu setting dengan 0,2 mol/L Na2HPO4 and 0,2 mol/L NaH2PO4 secara berturut-turut adalah 23,56±2,34 menit dan 14,12±2,01 menit. Uji T tidak berpasangan menunjukkan perbedaan waktu setting yang signifikan antara dua kelompok dengan 0,2 mol/L Na2HPO4 and 0,2 mol/L NaH2PO4 (p<0,05). Dengan demikian dapat disimpulkan bahwa semen α-TCP dengan cairan NaH2PO4 memiliki waktu setting yang lebih cepat karena pH cairan yang asam, sehingga proses disolusi berlangsung lebih cepat.

Calcium phosphate cements are widely researched as biomaterials for bone augmentation and regeneration. Alpha tricalcium phosphate (α-TCP) is one of example of calcium phosphate cements. It has some advantages, such as mouldable, in vivo hardening, and biocompatible. Setting of α-TCP cements starts immediately after mixing of the cement paste and cement is set after a few minutes. Setting time of α-TCP cements is influenced by several factors, for example type of liquid as α-TCP powder mixture. In this study, effect of phosphate solution on setting time α-TCP cement was investigated by employing two phosphate solution: 0.2 mol/L Na2HPO4 and 0.2 mol/L NaH2PO4. The cement powder (500 mg) was mixed in a glass plate with liquid (250 μl). After 1 min of mixing at room temperature the paste was applied in Teflon mould with an inner diameter of 10 mm and a height of 2.5 mm. The initial setting time at 37oC were determined with Gillmore needle. Mean and standard deviation of setting time with 0.2 mol/L Na2HPO4 and 0.2 mol/L NaH2PO4 respectively are 23.56±2.34 minutes and 14.12±2.01 minutes. Independent T-Test showed significant effect between two groups on the setting time with 0.2 mol/L Na2HPO4 and 0.2 mol/L NaH2PO4 (p<0,05). It was concluded that α-TCP cement with NaH2PO4 solution had faster setting time because the acidic pH of the solution so the dissolution process occurs earlier.

Kata Kunci : α-TCP, Na2HPO4, NaH2PO4, waktu setting