EFEK SAMPING LAMA APLIKASI DARI BLEACHING AGENT HIDROGEN PEROKSIDA 40% TERHADAP KEKASARAN PERMUKAAN RESIN KOMPOSIT TIPE NANOFIL

IZFAN YULVIANSYAH, Dr.drg. Widjijono, SU.

2013 | Skripsi | PENDIDIKAN DOKTER GIGI

Bleaching merupakan suatu perawatan gigi secara kimiawi pada gigi vital dan non vital yang mengalami diskolorasi. Salah satu teknik bleaching adalah teknik in office bleaching yang dilakukan dokter gigi di tempat praktek. Seringkali, aplikasi bleaching agent tidak hanya menyentuh jaringan gigi yang sehat, tetapi juga berpotensi menyentuh tumpatan pada gigi, contohnya resin komposit nanofil. Tujuan dari penelitian ini adalah untuk mengetahui adanya efek samping lama aplikasi dari bleaching agent hidrogen peroksida 40% terhadap kekasaran permukaan restorasi resin komposit tipe nanofil. Penelitian dilakukan dengan metode eksperimental laboratoris. Sampel penelitian adalah sampel resin komposit nanofil (Filtek Z350, 3M, USA) berbentuk cakram dengan ukuran diameter 10 mm dan tinggi 2 mm. Sampel dibuat sebanyak 12 sampel dan dibagi menjadi 3 kelompok yang terdiri dari 4 sampel. Seluruh sampel direndam dalam akuades dan dimasukkan ke dalam inkubator selama 24 jam dengan suhu 37OC. Sampel-sampel tersebut diaplikasi dengan bleaching agent hidrogen peroksida 40% (Opalescense Boost, USA) pada suhu ruangan (25OC). Setiap kelompok perlakuan memiliki variasi waktu kontak yang berbeda dengan bleaching agent, yaitu: 30 menit, 45 menit, dan 60 menit. Kekasaran permukaan yang diukur adalah sebelum dan setelah aplikasi bleaching. Data delta (Δ) kekasaran permukaan dianalisis menggunakan one way ANOVA dan dilanjutkan dengan LSD0,05. Hasil penelitian menunjukkan rerata dan simpangan baku delta (Δ) kekasaran permukaan awal dan akhir resin komposit nanofil dengan waktu kontak 30 menit 0,040 ± 0,016 𝜇m; 45 menit 0,045 ± 0,025 𝜇m; dan 60 menit 0,125 ± 0,025 𝜇m. Uji one way ANOVA menunjukkan bahwa terdapat pengaruh yang bermakna pada lama aplikasi dari bleaching agent hidrogen peroksida 40% terhadap kekasaran permukaan resin komposit nanofil (p<0,05). Uji LSD0,05 menunjukkan terdapat perbedaan nilai yang signifikan antar delta (Δ) rerata kekasaran permukaan pada semua kelompok, kecuali antara kelompok 30 dengan 45 menit. Kesimpulan penelitian ini adalah terdapat efek samping lama aplikasi dari bleaching agent hidrogen peroksida 40% terhadap kekasaran permukaan resin komposit nanofil.

Bleaching is a dental treatment uses chemical on discolored vital and nonvital teeth. From many bleaching techniques, there is one name in office bleaching which performed in the dentist's office. Often, the application of bleaching agents does not only touch the healthy tooth tissue, yet it has the potential to touch the tooth tissue that has tooth restoration, for example is the nanofill composite resin. The purpose of this study is to determine the adverse effects of application time of bleaching agent 40% of hydrogen peroxide on the surface roughness of nanofill type composite resin restorations. The study was conducted by an experimental laboratory method. The sample was a nanofill composite resin sample (Filtek Z350, 3M, USA) discshaped with a diameter of 10 mm and a height of 2 mm. Samples were made with a total of 12 samples, which were divided into 3 treatment groups with each group consist of 4 samples. The samples was soaked in aquades and put into incubator for 24 hours at 37OC. The samples applied with bleaching agent 40% hydrogen peroxide (Opalescense Boost, USA) at room temperature (25OC). Each treatment group had a different variation of contact time with bleaching agent, which were: 30 minutes, 45 minutes, and 60 minutes. The surface roughness was measured before and after the application of bleaching agent. Then the data delta (Δ) of surface roughness were statistically analyzed using One-Way ANOVA followed by LSD0,05 significance test. Results showed the mean and standard deviation of delta (Δ) of the initial and final surface roughness of nanofill composite resin with 30 minutes of contact time was 0.040 ±0.016 𝜇m; 45 minutes was 0.045 ± 0.025 𝜇m; and 60 minutes was 0.125 ± 0.025 𝜇m. One-way ANOVA test showed that there is a significant effect on the time length of application of the bleaching agent 40% hydrogen peroxide on the surface roughness of nanofill composite resin (p <0,05). LSD0,05 test showed significant differences between the mean value of delta (Δ) surface roughness in all groups, except among groups of 30 to 45 minutes. The conclusion of this study is a side effect from the application of bleaching agent 40% hydrogen peroxide on the surface roughness of nanofill composite resin does exist.

Kata Kunci : Bleaching agent, Hidrogen peroksida 40%, Resin komposit nanofil, Lama aplikasi, Kekasaran permukaan