PENGARUH BENTUK DAN WAKTU BENTANGAN TERHADAP KEKUATAN TARIK ELASTIK LATEKS ORTODONTIK

AULIYA LUDFI F, drg. Wayan Ardhana, MS., Sp. Ort. (K)

2013 | Skripsi | PENDIDIKAN DOKTER GIGI

Elastik adalah komponen yang paling sering dipakai dalam perawatan ortodontik cekat. Aplikasi bentuk pembentangan elastik dalam rongga mulut berbeda-beda tergantung pada situasi klinis. Bentuk pembentangan elastik tersebut antara lain classic, triangular, rectangular, v shape, u shape, dan accordion. Tujuan penelitian ini untuk mengetahui pengaruh bentuk dan waktu bentangan elastik terhadap kekuatan elastik lateks ortodontik. Sembilan puluh buah elastik lateks merk Leone dengan diameter 9,5 mm dan dengan kekuatan 3,5 oz dibagi dalam 6 kelompok bentuk bentangan secara random yaitu classic, triangular, rectangular, v shape, u shape, dan accordion.. Tiap kelompok bentuk bentangan dibagi secara random menjadi 3 kelompok waktu yaitu 24 jam, 48 jam, dan 72 jam. Semua elastik dalam tiap kelompok diukur kekuatan awalnya dengan tension gauge, kemudian dibentangkan pada jig board sesuai dengan kelompok bentuk yang telah ditentukan. Elastik kemudian direndam dalam saliva buatan bersuhu 37° selama 24 jam, 48 jam, dan 72 jam dan diukur kekuatannya pada jam tersebut. Hasil pengukuran dianalisis menggunakan Friedman Test untuk mengetahui pengaruh waktu pembentangan dan Kruskal Wallis untuk mengetahui pengaruh bentuk bentangan. Hasil penelitian menunjukkan bahwa elastik kelompok classic menunjukkan penurunan kekuatan dari kekuatan awal yang signifikan setelah dibentangkan 48 dan 72 jam (p<0,05). Kelompok elastik selain classic menunjukkan penurunan kekuatan dari kekuatan awal yang signifikan setelah dibentangkan 24, 48 dan 72 jam (p<0,05). Kekuatan antara jam ke 24 dan 48, 24 dan 72, serta 48 dan 72 tidak ada perbedaan yang signifikan. Kekuatan elastik antar bentuk bentangan tidak menunjukkan perbedaan yang signifikan. Kesimpulan penelitian ini adalah tidak terdapat pengaruh bentuk bentangan terhadap kekuatan tarik elastik lateks dan terdapat pengaruh waktu pembentangan terhadap kekuatan tarik elastik lateks.

Elastics are frequently used as active components of fixed orthodontic appliances. The forms of the stretching elastics are based on clinical situation. The type of the stretching forms are classic, triangular, rectangular, v-shape, u-shape, and accordion. The purposes of this study were to investigate the effect of the forms and the stretching period to the tensile strength of latex elastics. Ninety elastics namely Leone 3.5 oz which have 9.5 mm each in diameter were randomly divided into 6 groups of the elastic forms. They were classic, triangular, rectangular, v-shape, u-shape, and accordion. Each groups was randomly divided into 3 groups of the stretching period; they are 24 hours, 48 hours, and 72 hours. Each initial forces of elastic was measured with the tension gauge and then stretched based on groups with the jig board. After that, the elastics were soaked and incubated in 37° C artificial saliva until 24, 48, and 72 hours. Then,their elasticity forces were measured. The data were analyzed by using the Kruskal Wallis to investigate the effect of the stretching form to the force of latex elastic and the Friedman Test to investigate the effect of the stretching period. This study confirms that there is statistically significant differences on elastic classic forces after 48 and 72 hours stretching and there is statistically significant differences on triangular, rectangular, v-shape, u-shape, and accordion elastic forces after 24, 48, and 72 hours stretching (p<0.05). However, there are statistically insignificant differences on elastics forces among 24 and 48 hours, 24 and 72 hours, 48 and 72 hours stretching. There is statistically insignificant differences of elastics force among the forms of stretching as well. This study gives two important findings. Firstly, there is no influence of the stretching forms to the tensile strength of latex elastics . Secondly, there is influence of the stretching period to tensile strength.

Kata Kunci : Elastik lateks, bentuk bentangan, waktu bentangan