PENURUNAN NILAI COD PADA LIMBAH CAIR INDUSTRI OBAT BERBAHAN HERBAL DENGAN METODE FOTODEGRADASI TERKATALISIS TiO2 DAN OKSIDASI OLEH KAPORIT

IKA FITRI KRISNASIWI, Prof. Dr. Endang Tri Wahyuni, M.S

2013 | Tesis | S2 Ilmu Kimia

Penelitian ini dilakukan guna memperoleh metode yang efektif untuk menurunkan nilai COD limbah cair Industri Obat Berbahan Herbal (IOBH). Metode yang dikaji adalah fotodegradasi terkatalisis TiO2, oksidasi dengan CaOCl dan gabungan kedua metode dengan urutan oksidasi-fotodegradasi serta fotodegradasi-oksidasi. Fotodegradasi senyawa organik dalam limbah cair IOBH dilakukan dengan meradiasi campuran limbah cair dan fotokatalis TiO2 dalam reaktor tertutup yang dilengkapi lampu UV. Pada metode ini, parameter yang dipelajari yakni pengaruh waktu penyinaran dan massa fotokatalis. Proses oksidasi dilakukan dengan mereaksikan limbah cair dengan CaOCl. Pada proses oksidasi, pengaruh waktu reaksi dan massa CaOCl juga dipelajari. Gabungan kedua metode dilakukan pada kondisi optimum dari masing masing metode. Efektivitas dari setiap proses digambarkan dalam penurunan nilai COD. Penentuan nilai COD dilakukan dengan metode refluks-volumetribikromatometri. Hasil penelitian menunjukkan bahwa proses fotodegradasi yang dilakukan selama 24 jam dengan massa fotokatalis 75 mg dapat menurunkan nilai COD secara maksimal dari 19.556,57 hingga 2.262,86 mg/L. Dengan menggunakan proses oksidasi, penurunan nilai COD secara maksimal menjadi 1.828,57 mg/L dapat dicapai dengan waktu reaksi 24 jam dan massa CaOCl sebesar 75 mg. Hasil tersebut jelas menunjukkan bahwa proses fotodegradasi kurang efektif dibandingkan dengan proses oksidasi dalam menurunkan nilai COD. Gabungan metode dengan urutan fotodegradasi-oksidasi menghasilkan penurunan COD menjadi 571,43 mg/L, dimana nilai tersebut masih di atas baku mutu yang ditetapkan pemerintah yakni dibawah 300 mg/L. Gabungan metode oksidasifotodegradasi dapat menurunkan nilai COD hingga 228,6 mg/L, yang telah memenuhi baku mutu. Gabungan metode dengan urutan oksidasi-fotodegradasi dapat disarankan untuk diaplikasikan dalam pengolahan limbah cair IOBH.

This study was conducted to obtain the effective method decreasing COD level of the waste water from herbal medicine industry. The investigated methods were photodegradation catalyzed by TiO2, oxidation using CaOCl as an oxidising agent, and the combination methods with the order of oxidation- photodegradation, and that of photodegradation-oxidation. The photodegradation of organic compounds in the waste water was carried out by irradiating the mixture of the wastewater and TiO2 photocatalyst in the close reactor equipped with the UV-lamp. In this process, the influence of irradiation time and photocatalyst mass were studied. The oxidation was carried out by reacting the waste water with CaOCl. In this oxidation, the reaction time and mass of CaOCl were also optimized. The combination of the two methods in decreasing the COD level was performed at the optimum conditions of each method. The effectiveness of the processes was represented as COD level decreasing. The determination of COD level was conducted using reflux-volumetric bichromatometry method. The research results showed that photodegradation for 24 h and with 75 mg of TiO2 gave the maximum effectiveness in decreasing COD level from 19,556.57 to 2,262.86 mg/L. Mean while using oxidation method, the maximum decreasing COD level, became 1,828.57 mg/L can be achieved when 24 h of time and 75 mg of CaOCl was applied. It was clear seen that the former was less effective in decreasing the COD level than the latter. The combination methods with order of photodegradation- oxidation result in decreasing COD level to be 571.43 mg/L, that is still higher than regulated. The combination methods with the order of oxidation- photodegradation can decrease the COD level into 228.6 mg/L which meets the index quality regulated by the government, i.e. below 300 mg/L. It is recommended to apply the combination methods with order oxidation- photodegradation for treatment wastewater of herbal medicine industry

Kata Kunci : fotodegradasi, oksidasi, limbah cair IOBH, TiO2, klorin.