PERBANDINGAN KEKUATAN TARIK ELASTIK ORTODONTIK LATEKS DAN NON LATEKS DALAM SALIVA BUATAN DENGAN pH DAN WAKTU YANG BERBEDA (Penelitian Experimental Laboratoris)

Widjiasri Sumekar, Drg. Sri Suparwitri, SU,Sp.Ort(K).,

2013 | Tesis | S2 Ortodonsia

Elastik ortodontik merupakan salah satu komponen aktif alat tambahan ortodontik yang terbuat dari lateks dan non lateks. Elastik ortodontik harus mempertahankan kekuatan yang tepat agar dapat menerapkan kekuatan ideal. Pemakaian di klinik menunjukkan elastik ortodontik cepat mengalami penurunan kekuatan tarik yang cukup besar. Penurunan kekuatan tarik elastik ortodontik dipengaruhi jenis bahan, pH dan suhu. Tujuan penelitian ini adalah untuk mengetahui perbandingan kekuatan tarik elastik ortodontik lateks dan non lateks dalam saliva buatan dengan pH dan waktu yang berbeda. Penelitian ini dilakukan pada 120 elastik ortodontik lateks dan non lateks merk GAC yang direndam dalam saliva buatan dengan pH 5, 7 dan 8 selama 1/2 jam, 1 jam, 3 jam dan 24 jam. Masing-masing kelompok perendaman terdiri dari 5 elastik ortodontik. Pengukuran kekuatan tarik dilakukan sebelum perendaman dan setelah perendaman menggunakan alat ukur eqiupment pearson electronic. Hasil penelitian dianalisa menggunakan anava 3 jalur dan multiple comparisions. Analisa statistik menggunakan anava 3 jalur menunjukkan bahwa jenis elastik ortodontik mempunyai nilai p sebesar 0,00 (p<0,05), pH saliva buatan menunjukkan tidak ada perbedaan bermakna dengan nilai p sebesar 0,05 (p=0,05) dan waktu mempunyai nilai p sebesar 0,00 (p<0,05). Sedangkan perbandingan kekuatan tarik elastik ortodontik lateks dan non lateks dalam interaksi antara jenis bahan, pH dan waktu yang berbeda menunjukkan hasil tidak bermakna dengan nilai p sebesar 0,543 (p>0,05). Kesimpulan : Tidak ada perbedaan bermakna kekuatan tarik elastik ortodontik dalam interaksi antara jenis bahan elastik ortodontik, pH dan lama perendaman.

The orthodontic elastic was one of the active component of the additional orthodontic equipment which was made of latex and non latex. Orthodontic elastic had to keep a precise power up in order to supply the ideal power. Clinical application showed that orthodontic elastic had rapid great rapid descent force decay. The descent force decay of the orthodontic elastic was influenced by the kind of the material, the artificial pH saliva and the temperature. The purpose of this study was to know the comparison of the force decay of the orthodontic latex elastic and the non latex elastic in artificial pH saliva of different kinds and different time. This study was done to 120 orthodontic latex and non latex elastics soaked in artificial saliva with pH 5, 7 and 8 with length time halh an hour, an hour, three hours and twenty four hours. Each group of soaking consist of 5 orthodontic elastic. The measuring of the pulling power was done before and after the soaking, using the pearsons electronic equipment. The results of this study showed that the kind of orthodontic elastic had the grade of significance 0,00 (p<0,05). The grade of artificial pH saliva 0,05 (p=0,05). The grade of time 0,00 (p<0,05). The grade of the interaction of the kind of material and artificial pH saliva 0,04. Whereas the grade of the significance of the comparison of the pulling strength of orthodontic elastic latex and non latex artificial pH saliva in different kinds and different time didn’t show different significance 0,54 (p>0,05). The conclusion : There was no difference of the comparison of the force decay of the orthodontic latex and non latex in artificial pH saliva of different kinds and different times.

Kata Kunci : elastik ortodontik lateks, elastik ortodontik non lateks, kekuatan tarik, pH saliva buatan.