IMOBILISASI ASAM SALISILAT PADA Mg/Al HYDROTALCITE DAN APLIKASINYA UNTUK ADSORPSI-REDUKSI [AuCl4]ˉ

EKA ROVITA, Prof. Dr. Sri Juari Santosa, M.Eng

2013 | Tesis | S2 Ilmu Kimia

Aplikasi Mg/Al hydrotalcite-Asam Salisilat (HT-AS) untuk adsorpsireduksi [AuCl4]ˉ dalam larutan telah dilakukan. Mg/Al hydrotalcite disintesis dengan metode kopresipitasi langsung Mg(NO3)2 dan Al(NO3)3 pada pH 10,11 dengan perbandingan molar Mg(II) dan Al(III) 2 : 1. Padatan hasil sintesis dikarakterisasi menggunakan FTIR dan XRD, demikian juga dengan Mg/Al hydrotalcite yang telah terimobilisasi asam salisilat (HT-AS) dan setelah digunakan untuk adsorpsi-reduksi [AuCl4]ˉ. Aplikasi HT-AS sebagai adsorben untuk adsorpsi-reduksi [AuCl4]ˉ dipelajari dengan mengkaji pengaruh pH, kinetika dan isoterm adsorpsi serta pengaruh penambahan isopropanol. Logam Au yang terbentuk dikonfirmasi dengan difraktogram XRD. Imobilisasi asam salisilat pada Mg/Al hydrotalcite terjadi pada pH 5. Hasil analisis menggunakan FTIR dan XRD menunjukkan bahwa asam salisilat telah terimobilisasi pada permukaan Mg/Al hydrotalcite dengan kapasitas adsorpsi mengikuti model isoterm Langmuir sebesar 47,62 mg/g. Adsorpsi-reduksi [AuCl4]ˉ oleh adsorben HT-AS yang berlangsung optimum pada pH 3 mengikuti model kinetika pseudo orde dua Ho dan model isoterm Langmuir berturut-turut dengan konstanta laju reaksi (k) dan kapasitas adsorpsi masing-masing sebesar 1,1325 x 10-4 g/mg menit dan 166,67 mg/g. Hasil karakterisasi dengan XRD pada HT-AS setelah proses adsorpsi-reduksi [AuCl4]- menunjukkan bahwa Au(III) berhasil tereduksi menjadi Au(0) yang ditunjukkan dengan munculnya puncak karakteristik untuk Au(0) yaitu pada 2θ = 37,98 ; 44,19; dan 64,42. Penambahan isopropanol berpengaruh secara signifikan terhadap reduksi [AuCl4]ˉ menjadi Au(0) yang menunjukkan bahwa −OH memainkan peran dominan dalam reduksi [AuCl4]ˉ menjadi Au(0).

The application of Mg/Al hydrotalcite-Salicylic Acid (HT-AS) for the adsorption-reduction of [AuCl4]- in aqueous medium has been investigated. Mg/Al hydrotalcite was synthesized by direct coprecipitation method of Mg(NO3)2 and Al(NO3)3 at pH 10.11, with the molar ratio of Mg(II) to Al(III) 2:1 respectively. The synthesized Mg/Al hydrotalcite as well as its immobilization product with salicylic acid (HT-AS) before and after being used to adsorptionreduction [AuCl4]- were characterized by X-ray Diffraction and FT-IR Spectroscopy. The effect of pH adsorption-reduction [AuCl4]-, kinetic and isoterm adsorption, and effect of addition isopropanol as OH radical scavenger were also studied. The gold metal formed was confirmed by difractogram XRD. Immobilization of salicylic acid was reached at pH 5. The analytical result using FTIR and XRD showed that salicylic acid has been immobilized on surface of Mg/Al hydrotalcite with adsorption capacity which was determined according Langmuir isoterm model was 47.62 mg/g. Adsorption-reduction [AuCl4]ˉ by HTAS was optimum at pH 3 and followed pseudo-second order kinetic model and Langmuir isotherm model with rate constant (k) and adsorption capacity were 1.1325 x 10-4 g/mg minute and 166.67 mg/g respectively. The characterization results of HT-AS using XRD instrument after adsorption-reduction process of [AuCl4]- showed Au(III) was successfully reduced to Au(0) which was indicated by the appearance of characteristic peaks for Au(0) at 2θ = 37.98; 44.19; and 64.42. The addition of isopropanol gave significant effect on the reduction of [AuCl4]ˉ to Au(0), showing that –OH have dominant role on the reduction of [AuCl4]ˉ to Au(0).

Kata Kunci : Mg/Al Hydrotalcite, asam salisilat, adsorpsi-reduksi, [AuCl4]-