PENGARUH VARIASI WAKTU SOLUTION HEAT TREATMENT DAN SUHU AGING PERLAKUAN PANAS T6 PADA CENTRIFUGALCASTING 400 RPM DENGAN GRAIN REFINER Al-TiB 7,5% TERHADAP SIFAT FISIS DAN MEKANIS PADUAN ALUMINIUM COR A356 VELG SEPEDA MOTOR

Yulfitra, Dr. Eng. Priyo Tri Iswanto, S.T., M.Eng.,

2013 | Tesis | S2 Teknik Mesin

Perkembangan industri aluminium lokal skala kecil dan menengah khususnya velg sepeda motor cukup pesat, tetapi masih ada kendala karena kualitas. Metode centrifugal casting dapat memperbaiki kualitas dibanding gravity casting. Teknik ini menggunakan gaya sentrifugal dihasilkan cetakan berbentuk silindris berputar untuk melemparkan logam cair ke dinding cetakan. Tujuan penelitian ini adalah mengetahui pengaruh variasi waktu solution heat treatment dan variasi suhu penuaan (aging) terhadap sifat fisis dan mekanis hasil coran. Dalam penelitian ini material dasar yang digunakan adalah paduan aluminium cor A356. Paduan aluminium cor A356 ini mengandung Silicon 8,06% dan Magnesium 0,16% sebagai unsur paduan utama. Proses pengecoran dilakukan pada pre-heating cetakan 250 oC dan temperatur penuangan (pouring) 750 oC dengan putaran 400 rpm ditambah 7,5 % inokulan Al-TiB. Proses selanjutnya daria penelitian ini adalah perlakuan panas T6 terhadap benda uji. Temperatur solution heat treatment yang digunakan adalah 540 oC dengan variasi waktu tahan (holding time) 30, 60, 120, 180 dan 240 menit dan variasi temperatur precipitation heat treatment 100 oC, 125 oC, 150 oC, 175 oC, 200 oC dengan waktu tahan selama 3 jam, mengacu kepada standar ASTM (2004). Hasil penelitian menunjukkan kekerasan, kekuatan tarik dan ketangguhan serta densitas hasil coran secara umum mengalami peningkatan. Peningkatan sifat fisis dan mekanis terjadi pada waktu tahan 120 menit perlakuan panas T6 dengan suhu aging 100 oC. Setelah proses perlakuan panas dan aging mempengaruhi sifat dan mekanis hasil coran dimana terlihat adanya perbedaan morfologi pada batas butir matrik aluminium, yaitu terbentuknya presipitat yang diduga adalah senyawa Mg2Si. Sementara itu, dari hasil pengamatan struktur mikro menunjukkan adanya perubahan bentuk dan ukuran butir akibat perlakuan panas T6 dan suhu aging.

The development of the local aluminum industry in particular small and medium sized wheel motorcycle fast enough. Despite rapid but there are still obstacles in terms of quality. One method used in order to improve the quality of the local motorcycle wheels are centrifugal casting method. Centrifugal casting uses centrifugal force generated by the rotating mold to cast the molten metal into the mold wall. One of the automotive products that can be produced by this method are two-wheeled vehicles wheels. The purpose of this study was to determine the influence of variation of solution heat treatment T6 time and temperature variations aging the results of physical and mechanical properties of cast aluminum alloy A356 castings motorcycle wheels. The material used was aluminium alloy A356. The main compositon of this material was 8,06% Silicon and 0,16% magnesium.The temperature of the casting (pouring) 750 °C, preheating the mold (mold) 250 °C, with rotation of 400 rpm. The addition of 7.5% Al-TiB into 5 kg cast aluminum alloy A356. Results foundry alloy made of ASTM standard specimens. The specimen is inserted into an electric furnace to T6 heat treatment temperature of 540 °C, variations in hold time 30, 60, 120, 180 and 240 minutes. Variations in precipitation heat treatment temperature 100 °C, 125 °C, 150 °C, 175 °C, 200 °C with a hold for 3 hours, referring to ASTM standards (2004). Results showed hardness, tensile strength and toughness, and density results in general castings have increased. Improved physical and mechanical resistance occurred at 120 minutes with a T6 heat treatment temperature of 100 oC aging. After heat treatment and aging process affects the mechanical properties and the results of castings where morphological differences seen in the aluminum matrix grain boundaries, which is believed to be the formation of precipitates Mg2Si compound. Meanwhile, the results of microstructural observations indicate a change in the shape and size of the grain due to T6 heat treatment and aging temperature

Kata Kunci : Velg, centrifugal casting, Heat Treatment T6, aging.